Hydrolytic degradation of a resin composite as a function of the curing tip distance and aging
The influence of curing tip distance and storage time on the hardness of a composite was evaluated. Composite samples (Filtek Z250) were polymerized at different distances (5, 10, and 15 mm), compared with a control group (0 mm), and stored in distilled water at 37 ° C for 24 hours. The Knoop-hardne...
Main Authors: | Nádia da Rocha Svizero, Vanessa de Freitas Carvalho, Janaina Bechtold, Roberta Caroline Bruschi Alonso, Maria Teresa Atta, Paulo Henrique Perlatti D'Alpino |
---|---|
Format: | Article |
Language: | English |
Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2011-12-01
|
Series: | Materials Research |
Subjects: | |
Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392011000400019 |
Similar Items
-
Kinetic of water diffusion and color stability of a resin composite as a function of the curing tip distance
by: Nádia da Rocha Svizero, et al.
Published: (2012-08-01) -
Influence of Novel Experimental Light-Cured Resin Cement on Microtensile Bond Strength
by: Midori Kawamura, et al.
Published: (2022-09-01) -
Change of Microstructure and Hardness of Duo-Casted Al3003/Al4004 Clad Material during Extrusion Process
by: Jin-Kyung Lee, et al.
Published: (2020-12-01) -
Lamination and Its Impact on the Physical and Mechanical Properties of the Permian and Triassic Terrestrial Sandstones
by: Beata Figarska-Warchoł, et al.
Published: (2021-05-01) -
Analysis of residual stress in 1.4539 austenitic steel joints welded with TIG method
by: Barbara Nasiłowska, et al.
Published: (2019-03-01)