Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion
Concrete structure will be corroded under acid rain scouring and soaking for a long time, which has a great influence on its durability life. In order to further study the damage characteristics of fiber reinforced concrete under acid rain erosion, the formation mechanism of acid rain and its influe...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2020-01-01
|
| Series: | E3S Web of Conferences |
| Online Access: | https://www.e3s-conferences.org/articles/e3sconf/pdf/2020/58/e3sconf_isceg2020_01010.pdf |
| _version_ | 1818668109818494976 |
|---|---|
| author | Wu Duo |
| author_facet | Wu Duo |
| author_sort | Wu Duo |
| collection | DOAJ |
| description | Concrete structure will be corroded under acid rain scouring and soaking for a long time, which has a great influence on its durability life. In order to further study the damage characteristics of fiber reinforced concrete under acid rain erosion, the formation mechanism of acid rain and its influence on the corrosion and deterioration of concrete and fiber materials were analyzed in this paper. Taking basalt fiber concrete as an example, the characteristics such as porosity, compressive strength and mechanical indexes were studied and analyzed. Moreover, the reasons for the optimal fiber content was briefly analyzed. The results show that the inner structure of basalt concrete mixed with 0.1% fiber was the most stable and the corrosion resistance was the most satisfying.This conclusion has certain reference significance for the corrosion damage research of fiber reinforced concrete. |
| first_indexed | 2024-12-17T06:31:06Z |
| format | Article |
| id | doaj.art-30ba4408921e4247a681d3a85689dfa6 |
| institution | Directory Open Access Journal |
| issn | 2267-1242 |
| language | English |
| last_indexed | 2024-12-17T06:31:06Z |
| publishDate | 2020-01-01 |
| publisher | EDP Sciences |
| record_format | Article |
| series | E3S Web of Conferences |
| spelling | doaj.art-30ba4408921e4247a681d3a85689dfa62022-12-21T22:00:08ZengEDP SciencesE3S Web of Conferences2267-12422020-01-011980101010.1051/e3sconf/202019801010e3sconf_isceg2020_01010Study on Damage Characteristics of Fiber Concrete under Acid Rain ErosionWu Duo0Department of Civil Engineering, Nanchang Institute of TechnologyConcrete structure will be corroded under acid rain scouring and soaking for a long time, which has a great influence on its durability life. In order to further study the damage characteristics of fiber reinforced concrete under acid rain erosion, the formation mechanism of acid rain and its influence on the corrosion and deterioration of concrete and fiber materials were analyzed in this paper. Taking basalt fiber concrete as an example, the characteristics such as porosity, compressive strength and mechanical indexes were studied and analyzed. Moreover, the reasons for the optimal fiber content was briefly analyzed. The results show that the inner structure of basalt concrete mixed with 0.1% fiber was the most stable and the corrosion resistance was the most satisfying.This conclusion has certain reference significance for the corrosion damage research of fiber reinforced concrete.https://www.e3s-conferences.org/articles/e3sconf/pdf/2020/58/e3sconf_isceg2020_01010.pdf |
| spellingShingle | Wu Duo Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion E3S Web of Conferences |
| title | Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion |
| title_full | Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion |
| title_fullStr | Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion |
| title_full_unstemmed | Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion |
| title_short | Study on Damage Characteristics of Fiber Concrete under Acid Rain Erosion |
| title_sort | study on damage characteristics of fiber concrete under acid rain erosion |
| url | https://www.e3s-conferences.org/articles/e3sconf/pdf/2020/58/e3sconf_isceg2020_01010.pdf |
| work_keys_str_mv | AT wuduo studyondamagecharacteristicsoffiberconcreteunderacidrainerosion |