ЦЕМЕНТИЙН ГИДРАТЖИЛТЫН БҮТЭЭГДЭХҮҮНД НАНОЦАХИУРЫН ОКСИД НЭМЭЛТИЙН ҮЗҮҮЛЭХ НӨЛӨӨ
Addition of nano-silica effected to increase the content of calcium hydrasilicate and to decrease the content of calcium oxide for resulting the hydrate cement. Additional mass percent of nanosilica in all three cements of 1.0 % was important to increase compressive strength because the formation of...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Mongolian Academy of Sciences
2017-08-01
|
| Series: | Proceedings of the Mongolian Academy of Sciences |
| Subjects: | |
| Online Access: | https://www.mongoliajol.info/index.php/PMAS/article/view/847 |
| Summary: | Addition of nano-silica effected to increase the content of calcium hydrasilicate and to decrease the content of calcium oxide for resulting the hydrate cement. Additional mass percent of nanosilica in all three cements of 1.0 % was important to increase compressive strength because the formation of calcium hydrasilicate is increased and the content of calcium oxide is decreased which were become from the results of X-ray diffraction analysis. Therefore, the addition of nanosilica of 1.0 % is optimal dosage. This is related to the dissolution of calcium hydroxide |
|---|---|
| ISSN: | 2310-4716 2312-2994 |