High Manganese TWIP Steel with Increased Corrosion Resistance
The paper describes the development of austenitic steel with the TWIP effect, which is alloyed with chromium to increase corrosion resistance. The experimental heat of this steel was cast in an experimental melting furnace and subsequently subjected to hot and cold rolling. After cold rolling, the a...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2022-10-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2075-4701/12/10/1765 |
| _version_ | 1797471293096853504 |
|---|---|
| author | Pavel Podany Tomas Gregor Tomas Studecky Crtomir Donik |
| author_facet | Pavel Podany Tomas Gregor Tomas Studecky Crtomir Donik |
| author_sort | Pavel Podany |
| collection | DOAJ |
| description | The paper describes the development of austenitic steel with the TWIP effect, which is alloyed with chromium to increase corrosion resistance. The experimental heat of this steel was cast in an experimental melting furnace and subsequently subjected to hot and cold rolling. After cold rolling, the appropriate recrystallization annealing temperature was applied to obtain the optimal austenitic grain size. X-ray diffraction proved that the steel contains a fully austenitic structure. After recrystallization annealing, the sheets achieved a TS of more than 950 MPa with an elongation of 40%. The corrosion resistance of this steel is increased with the addition of chromium. |
| first_indexed | 2024-03-09T19:47:05Z |
| format | Article |
| id | doaj.art-3300abf9bcd04014a0828ffe843fdfae |
| institution | Directory Open Access Journal |
| issn | 2075-4701 |
| language | English |
| last_indexed | 2024-03-09T19:47:05Z |
| publishDate | 2022-10-01 |
| publisher | MDPI AG |
| record_format | Article |
| series | Metals |
| spelling | doaj.art-3300abf9bcd04014a0828ffe843fdfae2023-11-24T01:20:23ZengMDPI AGMetals2075-47012022-10-011210176510.3390/met12101765High Manganese TWIP Steel with Increased Corrosion ResistancePavel Podany0Tomas Gregor1Tomas Studecky2Crtomir Donik3Department of Materials Analysis, COMTES FHT a.s., Prumyslova 995, 334 41 Dobrany, Czech RepublicDepartment of Materials Analysis, COMTES FHT a.s., Prumyslova 995, 334 41 Dobrany, Czech RepublicDepartment of Metallurgical Technologies, COMTES FHT a.s., Prumyslova 995, 334 41 Dobrany, Czech RepublicDepartment of Physics and Chemistry of Materials, IMT—Institute of Metals and Technology, Lepi Pot 11, 1000 Ljubljana, SloveniaThe paper describes the development of austenitic steel with the TWIP effect, which is alloyed with chromium to increase corrosion resistance. The experimental heat of this steel was cast in an experimental melting furnace and subsequently subjected to hot and cold rolling. After cold rolling, the appropriate recrystallization annealing temperature was applied to obtain the optimal austenitic grain size. X-ray diffraction proved that the steel contains a fully austenitic structure. After recrystallization annealing, the sheets achieved a TS of more than 950 MPa with an elongation of 40%. The corrosion resistance of this steel is increased with the addition of chromium.https://www.mdpi.com/2075-4701/12/10/1765TWIPcold/hot rollingmechanical propertiescorrosion |
| spellingShingle | Pavel Podany Tomas Gregor Tomas Studecky Crtomir Donik High Manganese TWIP Steel with Increased Corrosion Resistance Metals TWIP cold/hot rolling mechanical properties corrosion |
| title | High Manganese TWIP Steel with Increased Corrosion Resistance |
| title_full | High Manganese TWIP Steel with Increased Corrosion Resistance |
| title_fullStr | High Manganese TWIP Steel with Increased Corrosion Resistance |
| title_full_unstemmed | High Manganese TWIP Steel with Increased Corrosion Resistance |
| title_short | High Manganese TWIP Steel with Increased Corrosion Resistance |
| title_sort | high manganese twip steel with increased corrosion resistance |
| topic | TWIP cold/hot rolling mechanical properties corrosion |
| url | https://www.mdpi.com/2075-4701/12/10/1765 |
| work_keys_str_mv | AT pavelpodany highmanganesetwipsteelwithincreasedcorrosionresistance AT tomasgregor highmanganesetwipsteelwithincreasedcorrosionresistance AT tomasstudecky highmanganesetwipsteelwithincreasedcorrosionresistance AT crtomirdonik highmanganesetwipsteelwithincreasedcorrosionresistance |