Fractography of Stress Corrosion Cracking of 20% Cold Worked Type 304 H Stainless Steel Containing δ-Ferrite in Oxidizing Primary Water
Fractography of stress corrosion cracking (SCC) of 20% cold worked Type 304 H stainless steel containing δ-ferrite was studied using a compact tension (CT) specimen in oxidizing primary water with a scanning electron microscope (SEM) and electron back scattered diffraction (EBSD). The stress corrosi...
Main Authors: | Hong-Pyo Kim, Jong-Yeon Lee, Sung-Hwan Cho, Min-Jae Choi, Sung-Woo Kim, Hyung-Ha Jin, Dong-Jin Kim, Seoung-Sik Hwang, Yun-Soo Lim |
---|---|
Format: | Article |
Language: | English |
Published: |
Polish Academy of Sciences
2024-04-01
|
Series: | Archives of Metallurgy and Materials |
Subjects: | |
Online Access: | https://journals.pan.pl/Content/130911/PDF/AMM-2024-1-09-Yun-Soo%20Lim.pdf |
Similar Items
-
Integrity Assessment of Stress Corrosion Cracking Susceptibility of Duplex UNS S32205 and Austenitic UNS S31653 Stainless Steel Reinforcements
by: Ulises Martin, et al.
Published: (2023-11-01) -
Fractography - microscopic cracking processes : a symposium... /
by: 471929 Symposium on Fractography - Microscopic Cracking Processes (1975 : Montreal), et al.
Published: (1976) -
Effect of High Temperature Oxidation on Infrared Irradiation of Stainless Steel 304
Published: (2020-02-01) -
The Corrosion Susceptibility of 304L Stainless Steel Exposed to Crevice Environments
by: Kun-Chao Tsai, et al.
Published: (2022-04-01) -
Effect of Heat Treatment on the Mechanical Properties of Stainless Steel 304
by: Nadhm Ibraheem Nasar
Published: (2017-12-01)