High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid
<p>Abstract</p> <p>Reduced graphene oxide-nanocrystalline platinum (RGO-Pt) hybrid materials were synthesized by simultaneous co-reduction of graphene oxide (GO) and chloroplatinic acid with sodium citrate in water at 80°C, of pH 7 and 10. The resultant RGO-Pt hybrid mater...
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
SpringerOpen
2011-01-01
|
Series: | Nanoscale Research Letters |
Online Access: | http://www.nanoscalereslett.com/content/6/1/241 |
_version_ | 1797761902288306176 |
---|---|
author | Wang Yinjie Liu Jincheng Liu Lei Sun Darren |
author_facet | Wang Yinjie Liu Jincheng Liu Lei Sun Darren |
author_sort | Wang Yinjie |
collection | DOAJ |
description | <p>Abstract</p> <p>Reduced graphene oxide-nanocrystalline platinum (RGO-Pt) hybrid materials were synthesized by simultaneous co-reduction of graphene oxide (GO) and chloroplatinic acid with sodium citrate in water at 80°C, of pH 7 and 10. The resultant RGO-Pt hybrid materials were characterized using transmission electron microscopy (TEM), powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy, and thermogravimetric analysis. Platinum (Pt) nanoparticles were anchored randomly onto the reduced GO (RGO) sheets with average mean diameters of 1.76 (pH 7) and 1.93 nm (pH 10). The significant Pt diffraction peaks and the decreased intensity of (002) peak in the XRD patterns of RGO-Pt hybrid materials confirmed that the Pt nanoparticles were anchored onto the RGO sheets and intercalated into the stacked RGO layers at these two pH values. The Pt loadings for the hybrid materials were determined as 36.83 (pH 7) and 49.18% (pH 10) by mass using XPS analysis. With the assistance of oleylamine, the resultant RGO-Pt hybrid materials were soluble in the nonpolar organic solvents, and the dispersion could remain stable for several months.</p> |
first_indexed | 2024-03-12T19:20:42Z |
format | Article |
id | doaj.art-365287a25af44fee9d6b37218a4b033a |
institution | Directory Open Access Journal |
issn | 1931-7573 1556-276X |
language | English |
last_indexed | 2024-03-12T19:20:42Z |
publishDate | 2011-01-01 |
publisher | SpringerOpen |
record_format | Article |
series | Nanoscale Research Letters |
spelling | doaj.art-365287a25af44fee9d6b37218a4b033a2023-08-02T05:11:25ZengSpringerOpenNanoscale Research Letters1931-75731556-276X2011-01-0161241High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acidWang YinjieLiu JinchengLiu LeiSun Darren<p>Abstract</p> <p>Reduced graphene oxide-nanocrystalline platinum (RGO-Pt) hybrid materials were synthesized by simultaneous co-reduction of graphene oxide (GO) and chloroplatinic acid with sodium citrate in water at 80°C, of pH 7 and 10. The resultant RGO-Pt hybrid materials were characterized using transmission electron microscopy (TEM), powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy, and thermogravimetric analysis. Platinum (Pt) nanoparticles were anchored randomly onto the reduced GO (RGO) sheets with average mean diameters of 1.76 (pH 7) and 1.93 nm (pH 10). The significant Pt diffraction peaks and the decreased intensity of (002) peak in the XRD patterns of RGO-Pt hybrid materials confirmed that the Pt nanoparticles were anchored onto the RGO sheets and intercalated into the stacked RGO layers at these two pH values. The Pt loadings for the hybrid materials were determined as 36.83 (pH 7) and 49.18% (pH 10) by mass using XPS analysis. With the assistance of oleylamine, the resultant RGO-Pt hybrid materials were soluble in the nonpolar organic solvents, and the dispersion could remain stable for several months.</p>http://www.nanoscalereslett.com/content/6/1/241 |
spellingShingle | Wang Yinjie Liu Jincheng Liu Lei Sun Darren High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid Nanoscale Research Letters |
title | High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid |
title_full | High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid |
title_fullStr | High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid |
title_full_unstemmed | High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid |
title_short | High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid |
title_sort | high quality reduced graphene oxide nanocrystalline platinum hybrid materials prepared by simultaneous co reduction of graphene oxide and chloroplatinic acid |
url | http://www.nanoscalereslett.com/content/6/1/241 |
work_keys_str_mv | AT wangyinjie highqualityreducedgrapheneoxidenanocrystallineplatinumhybridmaterialspreparedbysimultaneouscoreductionofgrapheneoxideandchloroplatinicacid AT liujincheng highqualityreducedgrapheneoxidenanocrystallineplatinumhybridmaterialspreparedbysimultaneouscoreductionofgrapheneoxideandchloroplatinicacid AT liulei highqualityreducedgrapheneoxidenanocrystallineplatinumhybridmaterialspreparedbysimultaneouscoreductionofgrapheneoxideandchloroplatinicacid AT sundarren highqualityreducedgrapheneoxidenanocrystallineplatinumhybridmaterialspreparedbysimultaneouscoreductionofgrapheneoxideandchloroplatinicacid |