Features of structure formation in nodular cast iron at horizontal continuous casting
Are studied features of graphite formation while melting cast iron and in castings 25 mm and 40 mm diameters. A new mechanism of graphitising innoculation is investigated.
Main Authors: | E. I. Marukovitch, V. Yu. Stetsenko, A. G. Solovey |
---|---|
Format: | Article |
Language: | English |
Published: |
Belarusian National Technical University
2000-05-01
|
Series: | Litʹë i Metallurgiâ |
Online Access: | https://lim.bntu.by/jour/article/view/2768 |
Similar Items
-
About an efficient innoculation of cast iron by bismuth
by: E. I. Marukovitch, et al.
Published: (2000-05-01) -
EVALUATION OF HEAT TRANSFER BETWEEN CASTING AND CRYSTALLIZER IN THE AREA OF FORMATION OF INITIAL SKIN AT CONTINUOUS HORIZONTAL CASTING OF CAST IRON
by: E. I. Marukovich, et al.
Published: (2007-02-01) -
Fracture analysis of nodular cast iron crankshaft
by: M. S. Xu, et al.
Published: (2020-01-01) -
Static and dynamic mechanical properties of nodular cast irons
by: A. Vaško, et al.
Published: (2019-03-01) -
On nucleation of graphite in cast iron
by: E. I. Marukovich, et al.
Published: (2000-11-01)