| Summary: | In the present research, the carbon fiber reinforced thermoplastic (CFRTP) was laser joined with the Al alloy whose joining interface was pretreated by laser micro-texturing, anodizing, and hybrid of laser micro-texturing and anodizing. The surface morphology of the pretreated Al joining interface and bonding strength of the corresponding Al/CFRTP butt joint were investigated. The results show that the laser micro-texturing has fabricated the micro-pit or micro-furrow in the Al joining interface. With the increasing of laser scanning times, the size of the micro-pit or micro-furrow decreases, when the laser scanning distance is constant. The bonding strength of the Al/CFRTP butt joint with Al joining interface pretreated by micro-texturing fluctuates with the increasing of laser scanning distance and times, reaching the maximum value of 20 MPa at laser scanning distance of 0.1 mm and 1 time. The anodizing pretreatment has formed the Al<sub>2</sub>O<sub>3</sub> oxide layer on the Al joining interface. The Al/CFRTP butt joint with Al joining interface pretreated by anodizing obtains the maximum bonding strength of 11 MPa at anodizing time of 10 min. The hybrid pretreatment of micro-texturing and subsequent anodizing fabricates the regular grid structure with smooth micro-furrow and micro-pit, while the hybrid pretreatment of anodizing and subsequent micro-texturing fabricates the Al joining interface with explosive micro-pit and micro-furrow. The bonding strength of the Al/CFRTP butt joint with hybrid-pretreated Al joining interface is relative better than that of the Al/CFRTP butt joint with anodizing-pretreated Al joining interface but almost lower than that of the Al/CFRTP butt joint with micro-texturing pretreated Al joining interface. Such results should be attributed to the surface morphology of the Al joining interface.
|
|---|