Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP)
AZ31B magnesium alloy with initial grain size of 11.2 µm was grain refined using Equal Channel Angular Pressing (ECAP) the alloy was ECAP-processed up to 5-times at 473 K. As a result, the grains are refined to 2.1 µm after three ECAP passes, the elongation was increased to 84 % at 473 K and strain...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Unviversity of Technology- Iraq
2014-08-01
|
| Series: | Engineering and Technology Journal |
| Subjects: | |
| Online Access: | https://etj.uotechnology.edu.iq/article_99933_17bd57736d9c9525ccf02bd4347cd615.pdf |
| _version_ | 1797325639402913792 |
|---|---|
| author | Ziad Tariq Madhloom Azal R. Ismail |
| author_facet | Ziad Tariq Madhloom Azal R. Ismail |
| author_sort | Ziad Tariq Madhloom |
| collection | DOAJ |
| description | AZ31B magnesium alloy with initial grain size of 11.2 µm was grain refined using Equal Channel Angular Pressing (ECAP) the alloy was ECAP-processed up to 5-times at 473 K. As a result, the grains are refined to 2.1 µm after three ECAP passes, the elongation was increased to 84 % at 473 K and strain rate of 1×10-4 s-1 after ECAP up to 5-passes,. Large fracture elongations of 261% are obtained at 623 K and strain rate 2.45×10-4 s-1 for specimen made from 3 ECAR passes compared to 183% for the as received material. Also the superplastic properties of the ECAP-processed specimens were investigated at 623 K and the strain rate ranges from 2.45×10-4 s-1 to 1.2×10-3 s-1. The strain rate sensitivity were determined to be 0.33 |
| first_indexed | 2024-03-08T06:12:17Z |
| format | Article |
| id | doaj.art-391790496a944cfb816b8dd11811ba19 |
| institution | Directory Open Access Journal |
| issn | 1681-6900 2412-0758 |
| language | English |
| last_indexed | 2024-03-08T06:12:17Z |
| publishDate | 2014-08-01 |
| publisher | Unviversity of Technology- Iraq |
| record_format | Article |
| series | Engineering and Technology Journal |
| spelling | doaj.art-391790496a944cfb816b8dd11811ba192024-02-04T17:31:17ZengUnviversity of Technology- IraqEngineering and Technology Journal1681-69002412-07582014-08-013281958197010.30684/etj.32.8A699933Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP)Ziad Tariq MadhloomAzal R. IsmailAZ31B magnesium alloy with initial grain size of 11.2 µm was grain refined using Equal Channel Angular Pressing (ECAP) the alloy was ECAP-processed up to 5-times at 473 K. As a result, the grains are refined to 2.1 µm after three ECAP passes, the elongation was increased to 84 % at 473 K and strain rate of 1×10-4 s-1 after ECAP up to 5-passes,. Large fracture elongations of 261% are obtained at 623 K and strain rate 2.45×10-4 s-1 for specimen made from 3 ECAR passes compared to 183% for the as received material. Also the superplastic properties of the ECAP-processed specimens were investigated at 623 K and the strain rate ranges from 2.45×10-4 s-1 to 1.2×10-3 s-1. The strain rate sensitivity were determined to be 0.33https://etj.uotechnology.edu.iq/article_99933_17bd57736d9c9525ccf02bd4347cd615.pdfsuperplasticitymagnesium alloysevere plastic deformation |
| spellingShingle | Ziad Tariq Madhloom Azal R. Ismail Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) Engineering and Technology Journal superplasticity magnesium alloy severe plastic deformation |
| title | Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) |
| title_full | Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) |
| title_fullStr | Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) |
| title_full_unstemmed | Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) |
| title_short | Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) |
| title_sort | superplastic behavior of az31b magnesium alloy processed by equal channel angular pressing ecap |
| topic | superplasticity magnesium alloy severe plastic deformation |
| url | https://etj.uotechnology.edu.iq/article_99933_17bd57736d9c9525ccf02bd4347cd615.pdf |
| work_keys_str_mv | AT ziadtariqmadhloom superplasticbehaviorofaz31bmagnesiumalloyprocessedbyequalchannelangularpressingecap AT azalrismail superplasticbehaviorofaz31bmagnesiumalloyprocessedbyequalchannelangularpressingecap |