| Summary: | The current investigation involved casting the Mg–2.2Gd–2.2Zn–0.2Ca (wt%) alloy (GZX220) through permanent mold casting, followed by homogenization at 400 °C for 24 h and extrusion at 250 °C, 300 °C, 350 °C, and 400 °C. Microstructure investigations revealed that α-Mg, Mg–Gd, and Mg–Gd–Zn intermetallic phases were present in the as-cast alloy. Following the homogenization treatment, a majority of these intermetallic particles underwent partial dissolution into the matrix phase. α-Mg grains exhibited a considerable refinement by extrusion due to dynamic recrystallization (DRX). At low extrusion temperatures, higher basal texture intensities were observed. The mechanical properties were remarkably enhanced after the extrusion process. However, a consistent decline in strength was observed with the rise in extrusion temperature. The corrosion performance of the as-cast GZX220 alloy was reduced by homogenization because of the lack of corrosion barrier effect of secondary phases. A significant enhancement of corrosion resistance was achieved by the extrusion process.
|
|---|