| Summary: | The properties of H<sub>2</sub>S gas sensing were investigated using a ZnO nanostructure prepared with AZO (zinc oxide with aluminium) and Al surfaces which were developed on a MEMS (Micro Electromechanical System) device. Hydrothermal synthesis was implemented for the deposition of the ZnO nanostructure. To find the optimal conditions for H<sub>2</sub>S gas sensing, different ZnO growth times and different temperatures were considered and tested, and the results were analysed. At 250 °C and 90 min growth time, a ZnO sensor prepared with AZO and 40 nm Al recorded an 8.5% H<sub>2</sub>S gas-sensing response at a 200 ppb gas concentration and a 14% sensing response at a gas concentration of 1000 ppb. The dominant sensing response provided the optimal conditions for the ZnO sensor, which were 250 °C temperature and 90 min growth time. Gas sensor selectivity was tested with five different gases (CO, SO<sub>2</sub>, NO<sub>2</sub>, NH<sub>3</sub> and H<sub>2</sub>S) and the sensor showed great selectivity towards H<sub>2</sub>S gas.
|
|---|