| Summary: | This article discusses the problems of creating new compositions for ceramic tiles. There are two ways to process the composition of the molding material - dry and wet. A description of the wet processing method is given. The molding of the plastic mass is carried out by pressing to obtain a tile with a size of 50 x 150 mm. The molded product goes through the following stages of the technological regime: blowing in a drying stove with an increase in temperature from 25 °C to 700 °C for 3-4 hours. Further, at a speed of 15-20 degrees per minute, the temperature rises to 1050 0C and then the heat treatment continues for 30 minutes. After annealing, the product is cooled and tested.
|
|---|