The Characters of Mo-MoSi2 Functionally Graded Coating
Mo-MoSi2 functionally graded coating on Mo substrate is prepared by siliconizing technology. The characters of Mo-MoSi2 functionally graded coating are analyzed by SEM, EDS, GDS and XRD. The result shows that Mo-MoSi2 functionally graded coating is dense and smooth, without pore and crack defects, g...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
De Gruyter
2014-06-01
|
| Series: | High Temperature Materials and Processes |
| Subjects: | |
| Online Access: | https://doi.org/10.1515/htmp-2013-0046 |
| Summary: | Mo-MoSi2 functionally graded coating on Mo substrate is prepared by siliconizing technology. The characters of Mo-MoSi2 functionally graded coating are analyzed by SEM, EDS, GDS and XRD. The result shows that Mo-MoSi2 functionally graded coating is dense and smooth, without pore and crack defects, gradient coating and Mo matrix achieve good metallurgy bond. The silicon molybdenum atom ratios (Si/Mo) in functionally graded coating appear three changing regularities. When the Si/Mo of outer layer are from 6:1 to 2:1, the surface phase is constituted by MoSi2 and Si; when the Si/Mo of interlayer is about 2:1, the interlayer phase is constituted by MoSi2; when the Si/Mo of transitional layer are from 2:1 to 0:1, the transitional layer phase is constituted by Mo5Si3 and Mo. The phase structure of Mo-MoSi2 functionally graded coating from outside to inside is outer layer MoSi2 + Si, interlayer MoSi2 and transitional layer Mo5Si3 + Mo3Si three-layer structure. The thermodynamic calculation results are consistent with the experimental results substantially. |
|---|---|
| ISSN: | 0334-6455 2191-0324 |