Effect of the thermal modification and nano-ZnO impregnation on the deterioration of Caribbean pine wood
This study aimed to investigate the effect of thermal modification and nano-zinc oxide (nano-ZnO) particle impregnation on the deterioration of Caribbean pine wood under field conditions. Samples were thermally-modified at various temperature levels (control, 180 °C, 200 °C, and 220 °C). Nano-ZnO i...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universidad del Bío-Bío
2020-10-01
|
| Series: | Maderas: Ciencia y Tecnología |
| Subjects: | |
| Online Access: | https://revistas.ubiobio.cl/index.php/MCT/article/view/4243 |
| Summary: | This study aimed to investigate the effect of thermal modification and nano-zinc oxide (nano-ZnO) particle impregnation on the deterioration of Caribbean pine wood under field conditions. Samples were thermally-modified at various temperature levels (control, 180 °C, 200 °C, and 220 °C). Nano-ZnO impregnation was done with an aqueous solution at 1,5 % in an autoclave under two-steps of pressure and vacuum. Unmodified and thermally-modified, non-impregnated and nano-ZnO-impregnated samples were exposed to deterioration for five months in field tests. A deterioration index was used to evaluate the health condition of the samples. The mass loss and occurrence of termite tunnels in percentage were also determined. The nano-ZnO impregnation improved the resistance of unmodified wood to field-deterioration. The thermal modification at 180oC and 200ºC increased the wood deterioration and nano-ZnO impregnation did not improve their resistance. Unmodified and 220 ºC-modified samples had lower mass loss by xylophages than other thermal treatments regardless of the nanoparticle impregnation. The nano-ZnO impregnation decreases the occurrence of termite tunnels in unmodified, 200 ºC and 220 ºC-modified samples.
|
|---|---|
| ISSN: | 0717-3644 0718-221X |