Fabrication, Microstructure, and Microhardness at High Temperature of In Situ Synthesized Ti<sub>3</sub>Al/Al<sub>2</sub>O<sub>3</sub> Composites

Fabrication, Microstructure, and Microhardness at High Temperature of In Situ Synthesized Ti<sub>3</sub>Al/Al<sub>2</sub>O<sub>3</sub> Composites

In this study, in situ Al<sub>2</sub>O<sub>3</sub>-reinforced Ti<sub>3</sub>Al composite was fabricated after 8 h of milling and sintering at 850 °C. A mixture of TiO<sub>2</sub> and Al powders were mechanically milled in a planetary mill, cold-compact...