Heat Generation in NMC622 Coin Cells during Electrochemical Cycling: Separation of Reversible and Irreversible Heat Effects
The thermal behavior of a commercial lithium-ion cell with the cathode material LiNi<sub>0.6</sub>Mn<sub>0.2</sub>Co<sub>0.2</sub>O<sub>2</sub> (NMC622) was investigated during the cycling process using a Tian-Calvet calorimeter (C80, SETARAM Instrumen...
Main Authors: | Wenjiao Zhao, Magnus Rohde, Ijaz Ul Mohsin, Carlos Ziebert, Hans J. Seifert |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-11-01
|
Series: | Batteries |
Subjects: | |
Online Access: | https://www.mdpi.com/2313-0105/6/4/55 |
Similar Items
-
Combined Thermal Runaway Investigation of Coin Cells with an Accelerating Rate Calorimeter and a Tian-Calvet Calorimeter
by: Wenjiao Zhao, et al.
Published: (2022-02-01) -
Holistic Investigation of the Inert Thermal Treatment of Industrially Shredded NMC 622 Lithium-Ion Batteries and Its Influence on Selective Lithium Recovery by Water Leaching
by: Christin Stallmeister, et al.
Published: (2023-12-01) -
Thermophysical Characterization of a Layered P2 Type Structure Na<sub>0.53</sub>MnO<sub>2</sub> Cathode Material for Sodium Ion Batteries
by: Ijaz Ul Mohsin, et al.
Published: (2021-03-01) -
Effective upcycling of NMC 111 to NMC 622 cathodes by hydrothermal relithiation and Ni-enriching annealing
by: Krystal Davis, et al.
Published: (2024-07-01) -
Influence of Flow-Gas Composition on Reaction Products of Thermally Treated NMC Battery Black Mass
by: Christin Stallmeister, et al.
Published: (2023-05-01)