Improving Hydrophobicity of Tropical Hardwood along Axial Positions
Wood is hygroscopic and is considered dimensionally unstable materials when exposed to wet conditions. To increase the hydrophobicity of wood, this study focused on the modification of tropical hardwood (Triplochiton scleroxylon) along different positions of the stem using acetic anhydride The weig...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Joint Coordination Centre of the World Bank assisted National Agricultural Research Programme (NARP)
2021-11-01
|
| Series: | Journal of Applied Sciences and Environmental Management |
| Online Access: | https://www.ajol.info/index.php/jasem/article/view/217961 |
| Summary: | Wood is hygroscopic and is considered dimensionally unstable materials when exposed to wet conditions. To increase the hydrophobicity of wood, this study focused on the modification of tropical hardwood (Triplochiton scleroxylon) along different positions of the stem using acetic anhydride The weight percent gain (WPG) was determined and acetylation reaction was confirmed with FTIR. The dimensional stability of the wood was characterized by water absorption (WA), volumetric swelling (VS), anti-swelling efficiency (ASE), and water repellent efficiency (WRE). Data obtained were subjected to analysis of variance at α0.05. It was observed that the weight gain (WG) by acetylation increases along the axial position (base to top) of T. scleroxylon wood. IR-spectra confirmed properly the substitution of the acetyl group. The treatment resulted in a marked improvement in the WA and VS, ASE, and WRE of acetylated T. scleroxylon wood were also found to improve considerably from base to top of the wood. It could be said that the WPG and hydrophobicity increased, but the percentage of water absorption and volumetric swelling diminished. Hence, the modified wood showed good hydrophobicity and improved dimensional stability.
|
|---|---|