| Summary: | Infrared and Raman spectroscopies have been used to analyze two series of sodium silicoborate glasses with 10 % and 20 % of Na<sub>2</sub>O. The obtained results are in accordance with those found in literature when using Raman and Infrared spectroscopies, however here it has been analyze in more detail the Polimerization Index (IP) of both systems. It has been observed that IP decreases with B concentration except for low B content glasses. This result has been assigned to an incomplete melting of such glasses due to the high temperatures needed to obtain well-melting glasses. Finally, it has been analyzed the BO<sub>4</sub>/BO<sub>3</sub> ratio as a function of the Na<sub>2</sub>O concentration, showing that as it would be expected the high BO4 concentration appears when the Na<sub>2</sub>O concentration is between 0.3 – 0.4 in moles.<br><br>En este trabajo se han estudiado mediante espectroscopías IR y Raman dos series de vidrios del sistema SiO<sub>2</sub>-B<sub>2</sub>O<sub>3</sub>-Na<sub>2</sub>O con contenidos fijos del 10 y 20% de Na<sub>2</sub>O. Los resultados obtenidos en cuanto a la evolución de las bandas IR o Raman son concordantes con los encontrados en la bibliografía, sin embargo en este trabajo se estudian más a fondo dichos resultados sobre todo en relación al índice de polimerización (IP) de la estructura vítrea de sílice y su variación para cada sistema. Se ha comprobado cómo el IP disminuye al aumentar el contenido en Boro con la relación B/Si excepto para contenidos en B pequeños lo que en principio podría indicar que estos últimos vidrios no han sido fundidos correctamente y no se ha llegado a una completa homogenización de la mezcla vitrificable. Finalmente se ha analizado la relación BO<sub>4</sub>/BO<sub>3</sub> en función del contenido en Na<sub>2</sub>O observándose cómo el número de grupos BO<sub>4</sub> es mayor cuando el contenido en Na<sub>2</sub>O está comprendido entre 0.3 y 0.4 molar.
|
|---|