Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden
The purpose of this paper was to discuss the best coating technology of water-based coatings containing microcapsules, and the anti-aging and self-repairing properties of water-based coatings containing microcapsules. Urea-formaldehyde encapsulated Nippon water-based emulsion microcapsules were prep...
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-05-01
|
Series: | Applied Sciences |
Subjects: | |
Online Access: | https://www.mdpi.com/2076-3417/11/10/4662 |
_version_ | 1797533472897630208 |
---|---|
author | Xiaoxing Yan Wenting Zhao Xingyu Qian |
author_facet | Xiaoxing Yan Wenting Zhao Xingyu Qian |
author_sort | Xiaoxing Yan |
collection | DOAJ |
description | The purpose of this paper was to discuss the best coating technology of water-based coatings containing microcapsules, and the anti-aging and self-repairing properties of water-based coatings containing microcapsules. Urea-formaldehyde encapsulated Nippon water-based emulsion microcapsules were prepared, and water-based coatings containing microcapsules were prepared. The optical and mechanical properties of the coatings under different coating technologies were investigated. Under the best coating technology, the aging resistance and self-repairing performance of the coating film were investigated. Experimental results showed that coating technology had no effect on color aberration of the coating film. The coating technology with two coats of primer, three coats of topcoat, addition of microcapsules into primer, had excellent glossiness, shock resistance of 12.0 kg·cm, adhesion of 0 grade, and fracture elongation of 26.3%. Compared with the coating film without microcapsules, the coating with microcapsules had better aging resistance and self-repairing property, and the self-repairing rate was about 20.0%. Compared with the paint film with Dulux water-based emulsion microcapsules, the paint film with Nippon water-based emulsion microcapsules had a higher self-repairing rate. This study provides a technical basis for self-repairing water-based coatings. |
first_indexed | 2024-03-10T11:15:03Z |
format | Article |
id | doaj.art-42ddd3936ad94813a6e1e4a000c094c1 |
institution | Directory Open Access Journal |
issn | 2076-3417 |
language | English |
last_indexed | 2024-03-10T11:15:03Z |
publishDate | 2021-05-01 |
publisher | MDPI AG |
record_format | Article |
series | Applied Sciences |
spelling | doaj.art-42ddd3936ad94813a6e1e4a000c094c12023-11-21T20:27:39ZengMDPI AGApplied Sciences2076-34172021-05-011110466210.3390/app11104662Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on LindenXiaoxing Yan0Wenting Zhao1Xingyu Qian2Co-Innovation Center of Efficient Processing and Utilization of Forest Resources, Nanjing Forestry University, Nanjing 210037, ChinaCollege of Furnishings and Industrial Design, Nanjing Forestry University, Nanjing 210037, ChinaCollege of Furnishings and Industrial Design, Nanjing Forestry University, Nanjing 210037, ChinaThe purpose of this paper was to discuss the best coating technology of water-based coatings containing microcapsules, and the anti-aging and self-repairing properties of water-based coatings containing microcapsules. Urea-formaldehyde encapsulated Nippon water-based emulsion microcapsules were prepared, and water-based coatings containing microcapsules were prepared. The optical and mechanical properties of the coatings under different coating technologies were investigated. Under the best coating technology, the aging resistance and self-repairing performance of the coating film were investigated. Experimental results showed that coating technology had no effect on color aberration of the coating film. The coating technology with two coats of primer, three coats of topcoat, addition of microcapsules into primer, had excellent glossiness, shock resistance of 12.0 kg·cm, adhesion of 0 grade, and fracture elongation of 26.3%. Compared with the coating film without microcapsules, the coating with microcapsules had better aging resistance and self-repairing property, and the self-repairing rate was about 20.0%. Compared with the paint film with Dulux water-based emulsion microcapsules, the paint film with Nippon water-based emulsion microcapsules had a higher self-repairing rate. This study provides a technical basis for self-repairing water-based coatings.https://www.mdpi.com/2076-3417/11/10/4662microcapsulecoating technologywater-based coatingsproperties |
spellingShingle | Xiaoxing Yan Wenting Zhao Xingyu Qian Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden Applied Sciences microcapsule coating technology water-based coatings properties |
title | Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden |
title_full | Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden |
title_fullStr | Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden |
title_full_unstemmed | Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden |
title_short | Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden |
title_sort | effect of water based emulsion core microcapsules on aging resistance and self repairing properties of water based coatings on linden |
topic | microcapsule coating technology water-based coatings properties |
url | https://www.mdpi.com/2076-3417/11/10/4662 |
work_keys_str_mv | AT xiaoxingyan effectofwaterbasedemulsioncoremicrocapsulesonagingresistanceandselfrepairingpropertiesofwaterbasedcoatingsonlinden AT wentingzhao effectofwaterbasedemulsioncoremicrocapsulesonagingresistanceandselfrepairingpropertiesofwaterbasedcoatingsonlinden AT xingyuqian effectofwaterbasedemulsioncoremicrocapsulesonagingresistanceandselfrepairingpropertiesofwaterbasedcoatingsonlinden |