The Effect of Thermomechanical Processing Sequence on the Dispersoid Distribution and Final Mechanical Properties of Spray-Formed Al-Cu-Li Alloy
Controlling the formation of the β′ (Al<sub>3</sub>Zr) phase is pivotal for regulating the recrystallization and thus the mechanical properties of the spray formed 2195 (Al-Cu-Li) alloy. In a conventional “homogenization-extrusion” process, the precipitation of β′ is severely affected by...
Main Authors: | Yaru Ning, Xingchen Zhang, Yunjia Huang, Lipeng Ding, Xiuchuan Lei, Yaoyao Weng, Lingfei Cao, Ke Zhang, Zhihong Jia |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-11-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/12/11/1893 |
Similar Items
-
The Effects of Double-Step Homogenization on Precipitation Behavior of Al<sub>3</sub>Zr Dispersoids and Microstructural Evolution in 2196 Aluminum Alloy
by: Hongyu Zhou, et al.
Published: (2023-05-01) -
Effects of Manganese and Zirconium Dispersoids on Strain Localization in Aluminum Alloys
by: Elena Jover Carrasco, et al.
Published: (2021-01-01) -
The Influence of Cu Addition on Dispersoid Formation and Mechanical Properties of Al-Mn-Mg 3004 Alloy
by: Zhen Li, et al.
Published: (2018-03-01) -
Effects of CrxMo(0.2-x) addition on the dispersoids evolution and mechanical properties of Al–Cu–Mg–Ag–Mn alloy
by: Chuang Yu, et al.
Published: (2023-05-01) -
Characterization of Zr-Containing Dispersoids in Al–Zn–Mg–Cu Alloys by Small-Angle Scattering
by: Mohammad Taha Honaramooz, et al.
Published: (2023-01-01)