Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board
AbstractThe paper aimed at evaluating the feasibility and the properties of a new product which combines wood veneer and high-density polyethylene (HDPE) from post-consuming plastic bags. Three HDPE amounts were evaluated: 150g/m2, 250 g/m2 e 350 g/m2. The boards were manufactured using a single-ope...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2015-10-01
|
| Series: | Materials Research |
| Subjects: | |
| Online Access: | http://www.scielo.br/pdf/mr/v18n5/1516-1439-mr-18-5-994.pdf |
| _version_ | 1798013855709790208 |
|---|---|
| author | Emanuela Camargo de Barros Lustosa Cláudio Henrique Soares Del Menezzi Rafael Rodolfo de Melo |
| author_facet | Emanuela Camargo de Barros Lustosa Cláudio Henrique Soares Del Menezzi Rafael Rodolfo de Melo |
| author_sort | Emanuela Camargo de Barros Lustosa |
| collection | DOAJ |
| description | AbstractThe paper aimed at evaluating the feasibility and the properties of a new product which combines wood veneer and high-density polyethylene (HDPE) from post-consuming plastic bags. Three HDPE amounts were evaluated: 150g/m2, 250 g/m2 e 350 g/m2. The boards were manufactured using a single-opening hot-press under such conditions: 140ºC, for 20 minutes and pressure of 1 N/mm2. It was found that the production of this kind of composite board is technically possible and relatively simple and they did not present any veneer delamination. The properties of the composite boards were quite similar or even higher to those found in LVL made using thermosetting resin. The higher the HDPE amount the higher the density of the composite board, which imparted significantly in mechanical properties. However, when the composite boards were evaluated under same density the effect of the HDPE amount affected only Janka hardness. |
| first_indexed | 2024-04-11T15:09:16Z |
| format | Article |
| id | doaj.art-443ec194513b4ee2ba2b9ee8c61791f6 |
| institution | Directory Open Access Journal |
| issn | 1516-1439 |
| language | English |
| last_indexed | 2024-04-11T15:09:16Z |
| publishDate | 2015-10-01 |
| publisher | Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol) |
| record_format | Article |
| series | Materials Research |
| spelling | doaj.art-443ec194513b4ee2ba2b9ee8c61791f62022-12-22T04:16:42ZengAssociação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)Materials Research1516-14392015-10-0118599499910.1590/1516-1439.010615Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite BoardEmanuela Camargo de Barros LustosaCláudio Henrique Soares Del MenezziRafael Rodolfo de MeloAbstractThe paper aimed at evaluating the feasibility and the properties of a new product which combines wood veneer and high-density polyethylene (HDPE) from post-consuming plastic bags. Three HDPE amounts were evaluated: 150g/m2, 250 g/m2 e 350 g/m2. The boards were manufactured using a single-opening hot-press under such conditions: 140ºC, for 20 minutes and pressure of 1 N/mm2. It was found that the production of this kind of composite board is technically possible and relatively simple and they did not present any veneer delamination. The properties of the composite boards were quite similar or even higher to those found in LVL made using thermosetting resin. The higher the HDPE amount the higher the density of the composite board, which imparted significantly in mechanical properties. However, when the composite boards were evaluated under same density the effect of the HDPE amount affected only Janka hardness.http://www.scielo.br/pdf/mr/v18n5/1516-1439-mr-18-5-994.pdflaminated veneer lumberpost-consuming plastic bagrecycling |
| spellingShingle | Emanuela Camargo de Barros Lustosa Cláudio Henrique Soares Del Menezzi Rafael Rodolfo de Melo Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board Materials Research laminated veneer lumber post-consuming plastic bag recycling |
| title | Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board |
| title_full | Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board |
| title_fullStr | Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board |
| title_full_unstemmed | Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board |
| title_short | Production and Properties of a New Wood Laminated Veneer/High-Density Polyethylene Composite Board |
| title_sort | production and properties of a new wood laminated veneer high density polyethylene composite board |
| topic | laminated veneer lumber post-consuming plastic bag recycling |
| url | http://www.scielo.br/pdf/mr/v18n5/1516-1439-mr-18-5-994.pdf |
| work_keys_str_mv | AT emanuelacamargodebarroslustosa productionandpropertiesofanewwoodlaminatedveneerhighdensitypolyethylenecompositeboard AT claudiohenriquesoaresdelmenezzi productionandpropertiesofanewwoodlaminatedveneerhighdensitypolyethylenecompositeboard AT rafaelrodolfodemelo productionandpropertiesofanewwoodlaminatedveneerhighdensitypolyethylenecompositeboard |