Thickness Effect on Photocatalytic Activity of TiO<sub>2</sub> Thin Films Fabricated by Ultrasonic Spray Pyrolysis
In this study, TiO<sub>2</sub> thin films were deposited by ultrasonic spray pyrolysis from solutions with concentrations of 0.1 and 0.2 M. The deposition temperature was adjusted at 350 °C and all samples were annealed at 500 °C for 1 h in air. The thickness of TiO<sub>2</sub&g...
Main Authors: | Ibrahim Dundar, Arvo Mere, Valdek Mikli, Malle Krunks, Ilona Oja Acik |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-09-01
|
Series: | Catalysts |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4344/10/9/1058 |
Similar Items
-
Enhanced Visible and Ultraviolet Light-Induced Gas-Phase Photocatalytic Activity of TiO<sub>2</sub> Thin Films Modified by Increased Amount of Acetylacetone in Precursor Solution for Spray Pyrolysis
by: Jekaterina Spiridonova, et al.
Published: (2020-09-01) -
Low-cost plasmonic solar cells prepared by chemical spray pyrolysis
by: Erki Kärber, et al.
Published: (2014-12-01) -
Novel Effective Photocatalytic Self-Cleaning Coatings: TiO<sub>2</sub>-Polyfluoroalkoxy Coatings Prepared by Suspension Plasma Spraying
by: Chunyan He, et al.
Published: (2023-12-01) -
Synthesis and characterization of Eu3+ doped TiO2 thin films deposited by spray pyrolysis technique for photocatalytic application
by: S M AL-Shomar
Published: (2021-01-01) -
Green and Short Preparation of CeO<sub>2</sub> Nanoparticles with Large Specific Surface Area by Spray Pyrolysis
by: Yongfu Wu, et al.
Published: (2021-08-01)