| Summary: | A unique method to prepare Zn-P co-modified hierarchical ZSM-5 zeolites was developed. The ZSM-5 zeolite was directly synthesized by a dry gel conversion without adding any templates or seeds. Afterwards, the hierarchical structure was endowed to the ZSM-5 zeolite by the sequential desilication-dealumination. Zn and P species were then introduced into the hierarchical ZSM-5 zeolites by the impregnation method and their activity in methanol to aromatics process was investigated. It was found that the Zn-P co-modified hierarchical ZSM-5 zeolites possessed more Zn-related Lewis acid sites, and the ratio of Zn(OH)<sup>+</sup>/ZnO was increased. The catalytic evaluation results revealed that the benzene, toluene and xylene (BTX) and aromatics selectivity were significantly improved from 20.59% and 29.41% of pristine ZSM-5 zeolite to 28.12% and 41.88% of Zn-P co-modified hierarchical counterpart (1.5Zn0.3P/HZSM-5), respectively. Owing to the introduced highly stable Zn-P co-modified hierarchical structures, the lifetime (conversion not less than 99%) of ZSM-5 zeolite during methanol to aromatics reaction was increased from 6 h to 18 h.
|
|---|