In-Situ X-Ray CT Characterization of Damage Mechanism of Plain Weave SiCf/SiC Composites Under Compression
In order to reveal the damage evolution and failure mechanism of ceramic matrix composites (CMCs), in-situ X-ray CT compression tests of plain weave SiCf/SiC composites were conducted, and the CT data during loading and after failure were obtained. Displacement and strain distributions of the materi...
Main Author: | CHENG Xiangwei, ZHANG Daxu, DU Yonglong, GUO Hongbao, HONG Zhiliang |
---|---|
Format: | Article |
Language: | zho |
Published: |
Editorial Office of Journal of Shanghai Jiao Tong University
2024-02-01
|
Series: | Shanghai Jiaotong Daxue xuebao |
Subjects: | |
Online Access: | https://xuebao.sjtu.edu.cn/article/2024/1006-2467/1006-2467-58-2-232.shtml |
Similar Items
-
Interfacial structures evolution at hetero interfaces in SiCf/SiC | Nb | SiCf/SiC sandwich cladding structure
by: Hailong Qin, et al.
Published: (2023-09-01) -
Effects of pore characteristics on SiCf/SiC cladding equivalent Young's modulus
by: LI Yi, et al.
Published: (2021-10-01) -
Comparisons of Damage Evolution between 2D C/SiC and SiC/SiC Ceramic-Matrix Composites under Tension-Tension Cyclic Fatigue Loading at Room and Elevated Temperatures
by: Longbiao Li
Published: (2016-10-01) -
KD-S SiCf/SiC composites with BN interface fabricated by polymer infiltration and pyrolysis process
by: Honglei Wang, et al.
Published: (2018-03-01) -
Microstructures of a SiC–ZrC Ceramic Fiber Derived from a Polymeric Precursor
by: Min Ge, et al.
Published: (2020-05-01)