Abrasive Machining Characteristics and Prediction Model for Sisal/Polyester Sandwich Composite
This work focuses on optimization of abrasive machining parameters of the natural fiber reinforced sandwich composite, which is rarely reported in the literature. A sandwich made of vegetable fiber composite skins and polyvinyl chloride (PVC) foam of 80 gsm was machined for optimal conditions. The d...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Taylor & Francis Group
2022-10-01
|
| Series: | Journal of Natural Fibers |
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1080/15440478.2021.1958427 |
| Summary: | This work focuses on optimization of abrasive machining parameters of the natural fiber reinforced sandwich composite, which is rarely reported in the literature. A sandwich made of vegetable fiber composite skins and polyvinyl chloride (PVC) foam of 80 gsm was machined for optimal conditions. The design of experiment and analysis were adopted to confirm the influence of machining parameters. The machining characters of bio-sandwich were compared with synthetic and hybrid sandwich panels to optimize the machinability of the target. The panels were manufactured through vacuum infusion bagging. The machining studies were done using the abrasive water jet cutting machine. The machining characteristics were optimized for the parameters and L18 Taguchi technique was employed in parameter optimization. Three controlled levels of machining parameters were chosen to be optimized: standoff distance (SOD), abrasive water jet pressure (JP), and nozzle traverse rate (TR). The response of kerf taper (KT), surface roughness (SR), and material removal rate (MRR) were investigated. It is observed that highest levels of these parameters gave minimum kerf taper and lowest levels produce lower surface roughness. The surface roughness and damage on the surface was observed using scanning electron microscopy (SEM). It Shows that flowing abrasive particle’s directional distortion noted at the foam regions due to their higher damping nature. The prediction model shows a good agreement with the experimental value. |
|---|---|
| ISSN: | 1544-0478 1544-046X |