Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging
This study aims at investigation of the hydrogen damage after dissolution annealing and two-stage aging in aluminum 7075 alloy. Dissolution annealing was performed at 500 to 575 °C for duration of 1 to 20 hours. The first stage of two-stage aging was performed at 180, 200 and 220 °C...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | fas |
| Published: |
Isfahan University of Technology
2016-06-01
|
| Series: | Journal of Advanced Materials in Engineering |
| Subjects: | |
| Online Access: | http://jame.iut.ac.ir/browse.php?a_code=A-10-1-691&slc_lang=en&sid=1 |
| _version_ | 1818618088195620864 |
|---|---|
| author | S. Gholipour S.R. Hosseini R. Shoja Razavi |
| author_facet | S. Gholipour S.R. Hosseini R. Shoja Razavi |
| author_sort | S. Gholipour |
| collection | DOAJ |
| description | This study aims at investigation of the hydrogen damage after dissolution annealing and two-stage aging in aluminum 7075 alloy. Dissolution annealing was performed at 500 to 575 °C for duration of 1 to 20 hours. The first stage of two-stage aging was performed at 180, 200 and 220 °C for 30 minutes. The second stage was carried out at 120 and 150 °C for 10, 15 and 20 hours. Structural characteristics and chemical composition of precipitates was investigated using SEM and EDS methods, respectively. Reduction of the tensile strength in T6 process after hydrogenation reached to 150 MPa, although it decreased only, about 50 MPa in the two-stage process. Overall, tensile strength after hydrogen charging was significantly increased in the two-stage aging compared to the T6 process. |
| first_indexed | 2024-12-16T17:16:02Z |
| format | Article |
| id | doaj.art-4c8510387e6a43ef94f695ffa0f0a82d |
| institution | Directory Open Access Journal |
| issn | 1025-2851 2423-5733 |
| language | fas |
| last_indexed | 2024-12-16T17:16:02Z |
| publishDate | 2016-06-01 |
| publisher | Isfahan University of Technology |
| record_format | Article |
| series | Journal of Advanced Materials in Engineering |
| spelling | doaj.art-4c8510387e6a43ef94f695ffa0f0a82d2022-12-21T22:23:17ZfasIsfahan University of TechnologyJournal of Advanced Materials in Engineering1025-28512423-57332016-06-01351110Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage AgingS. Gholipour0S.R. Hosseini1R. Shoja Razavi2 Faculty of Materials Engineering, Malek Ashtar University of Technology, Shahin Shahr, Iran Faculty of Materials Engineering, Malek Ashtar University of Technology, Shahin Shahr, Iran Faculty of Materials Engineering, Malek Ashtar University of Technology, Shahin Shahr, Iran This study aims at investigation of the hydrogen damage after dissolution annealing and two-stage aging in aluminum 7075 alloy. Dissolution annealing was performed at 500 to 575 °C for duration of 1 to 20 hours. The first stage of two-stage aging was performed at 180, 200 and 220 °C for 30 minutes. The second stage was carried out at 120 and 150 °C for 10, 15 and 20 hours. Structural characteristics and chemical composition of precipitates was investigated using SEM and EDS methods, respectively. Reduction of the tensile strength in T6 process after hydrogenation reached to 150 MPa, although it decreased only, about 50 MPa in the two-stage process. Overall, tensile strength after hydrogen charging was significantly increased in the two-stage aging compared to the T6 process.http://jame.iut.ac.ir/browse.php?a_code=A-10-1-691&slc_lang=en&sid=1Two-stage aging Dissolution annealing Aluminum 7075 Hydrogen damage |
| spellingShingle | S. Gholipour S.R. Hosseini R. Shoja Razavi Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging Journal of Advanced Materials in Engineering Two-stage aging Dissolution annealing Aluminum 7075 Hydrogen damage |
| title | Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging |
| title_full | Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging |
| title_fullStr | Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging |
| title_full_unstemmed | Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging |
| title_short | Evaluation of Hydrogen Damage in Aluminum 7075 Alloy after Dissolution Annealing and Two-stage Aging |
| title_sort | evaluation of hydrogen damage in aluminum 7075 alloy after dissolution annealing and two stage aging |
| topic | Two-stage aging Dissolution annealing Aluminum 7075 Hydrogen damage |
| url | http://jame.iut.ac.ir/browse.php?a_code=A-10-1-691&slc_lang=en&sid=1 |
| work_keys_str_mv | AT sgholipour evaluationofhydrogendamageinaluminum7075alloyafterdissolutionannealingandtwostageaging AT srhosseini evaluationofhydrogendamageinaluminum7075alloyafterdissolutionannealingandtwostageaging AT rshojarazavi evaluationofhydrogendamageinaluminum7075alloyafterdissolutionannealingandtwostageaging |