Improvement in surface conditions of electroplated Fe-Pt thick-film magnets
Fe-Pt thick-films were electroplated on Ta, Ti, Co, Ni, and Cu plates (substrates) using a direct current, and the surface morphology, the magnetic properties, and the crystal structure of the films were evaluated. The films plated on the Co, Ni, and Cu substrates showed much smooth surface compared...
| Main Authors: | , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
AIP Publishing LLC
2018-05-01
|
| Series: | AIP Advances |
| Online Access: | http://dx.doi.org/10.1063/1.5007196 |
| _version_ | 1818947776140017664 |
|---|---|
| author | T. Yanai J. Honda R. Hamamura Y. Omagari H. Yamada N. Fujita K. Takashima M. Nakano H. Fukunaga |
| author_facet | T. Yanai J. Honda R. Hamamura Y. Omagari H. Yamada N. Fujita K. Takashima M. Nakano H. Fukunaga |
| author_sort | T. Yanai |
| collection | DOAJ |
| description | Fe-Pt thick-films were electroplated on Ta, Ti, Co, Ni, and Cu plates (substrates) using a direct current, and the surface morphology, the magnetic properties, and the crystal structure of the films were evaluated. The films plated on the Co, Ni, and Cu substrates showed much smooth surface compared with those for the Ta and Ti ones, and we confirmed that the Cu plate was the most attractive substrate due to very small cracks after an annealing for L10 ordering. High coercivity (>800 kA/m) for the Cu substrate is almost the same as that for our previous study in which we employed the Ta substrate, and we found that the Cu plate is a hopeful substrate to improve the surface conditions of electroplated Fe-Pt thick-film magnets. |
| first_indexed | 2024-12-20T08:36:16Z |
| format | Article |
| id | doaj.art-4cb11402608c4aaeaa57fbe87657bf37 |
| institution | Directory Open Access Journal |
| issn | 2158-3226 |
| language | English |
| last_indexed | 2024-12-20T08:36:16Z |
| publishDate | 2018-05-01 |
| publisher | AIP Publishing LLC |
| record_format | Article |
| series | AIP Advances |
| spelling | doaj.art-4cb11402608c4aaeaa57fbe87657bf372022-12-21T19:46:33ZengAIP Publishing LLCAIP Advances2158-32262018-05-0185056437056437-510.1063/1.5007196259892ADVImprovement in surface conditions of electroplated Fe-Pt thick-film magnetsT. Yanai0J. Honda1R. Hamamura2Y. Omagari3H. Yamada4N. Fujita5K. Takashima6M. Nakano7H. Fukunaga8Nagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanNagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanNagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanNagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanNational Institute of Technology, Nara College, 22 Yata-cho, Yamatokoriyama, Nara 639-1080, JapanNational Institute of Technology, Nara College, 22 Yata-cho, Yamatokoriyama, Nara 639-1080, JapanNagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanNagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanNagasaki University, 1-14 Bunkyo-Machi, Nagasaki 852-8521, JapanFe-Pt thick-films were electroplated on Ta, Ti, Co, Ni, and Cu plates (substrates) using a direct current, and the surface morphology, the magnetic properties, and the crystal structure of the films were evaluated. The films plated on the Co, Ni, and Cu substrates showed much smooth surface compared with those for the Ta and Ti ones, and we confirmed that the Cu plate was the most attractive substrate due to very small cracks after an annealing for L10 ordering. High coercivity (>800 kA/m) for the Cu substrate is almost the same as that for our previous study in which we employed the Ta substrate, and we found that the Cu plate is a hopeful substrate to improve the surface conditions of electroplated Fe-Pt thick-film magnets.http://dx.doi.org/10.1063/1.5007196 |
| spellingShingle | T. Yanai J. Honda R. Hamamura Y. Omagari H. Yamada N. Fujita K. Takashima M. Nakano H. Fukunaga Improvement in surface conditions of electroplated Fe-Pt thick-film magnets AIP Advances |
| title | Improvement in surface conditions of electroplated Fe-Pt thick-film magnets |
| title_full | Improvement in surface conditions of electroplated Fe-Pt thick-film magnets |
| title_fullStr | Improvement in surface conditions of electroplated Fe-Pt thick-film magnets |
| title_full_unstemmed | Improvement in surface conditions of electroplated Fe-Pt thick-film magnets |
| title_short | Improvement in surface conditions of electroplated Fe-Pt thick-film magnets |
| title_sort | improvement in surface conditions of electroplated fe pt thick film magnets |
| url | http://dx.doi.org/10.1063/1.5007196 |
| work_keys_str_mv | AT tyanai improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT jhonda improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT rhamamura improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT yomagari improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT hyamada improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT nfujita improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT ktakashima improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT mnakano improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets AT hfukunaga improvementinsurfaceconditionsofelectroplatedfeptthickfilmmagnets |