Effect of different cavity conditioners on microleakage of glass ionomer cement with a high viscosity in primary teeth
Background: Glass ionomer cement is a common material used in pediatric dentistry. The aim of this study was to evaluate the microleakage of high-viscosity glass ionomer restorations in deciduous teeth after conditioning with four different conditioners. Materials and Methods: Fifty intact primary...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wolters Kluwer Medknow Publications
2015-01-01
|
| Series: | Dental Research Journal |
| Subjects: | |
| Online Access: | http://www.drjjournal.net/article.asp?issn=1735-3327;year=2015;volume=12;issue=4;spage=337;epage=341;aulast=Mazaheri |
| Summary: | Background: Glass ionomer cement is a common material used in pediatric dentistry. The aim of this study was to evaluate the microleakage of high-viscosity glass ionomer restorations in deciduous teeth after conditioning with four different conditioners.
Materials and Methods: Fifty intact primary canines were collected. Standard Class V cavities (2 mm × 1.5 mm × 3 mm) were prepared by one operator on all buccal tooth surfaces, including both enamel and dentin. The samples were divided into five groups with different conditioners (no conditioner, 20% acrylic acid, 35% phosphoric acid, 12% citric acid, and 17% ethylenediaminetetraacetic acid [EDTA]). Two-way - ANOVA, Kruskal-Wallis and Mann-Whitney tests were used to compare the means of microleakage between the five groups. The significance level was set at P < 0.05.
Results: There was no significant difference between the means of microleakage in incisal (enamel) and gingival (dentin) margins (P = 0.34). Furthermore, there was no significant difference between the means of microleakage in enamel and dentin margins (P = 0.4). There was a significant difference between the means of microleakage in different groups (P = 0.03).
Conclusion: Within the limitations of this study, it is suggested that 20% acrylic acid and 17% EDTA be used for cavity conditioning which can result in better chemical and micromechanical adhesion. |
|---|---|