Structural Characterization of Low-Sr-Doped Hydroxyapatite Obtained by Solid-State Synthesis
Strontium-substituted Ca<sub>10</sub>(PO<sub>4</sub>)<sub>6</sub>(OH)<sub>2</sub> hydroxyapatite (HAp) powders, with Sr wt% concentrations of 2.5, 5.6 and 10%, were prepared by a solid-state synthesis method. The chemical composition of the samples was...