Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H
Selection of materials connecting rod for a component or structure usually involves several aspects, there are aspects of specific strength, stiffness, lightweight, noncorrosive materials and resistance or age. In the manufacturing process connecting rod always give heat treatment such as Normalizin...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Brawijaya
2019-01-01
|
| Series: | Rekayasa Mesin |
| Subjects: | |
| Online Access: | http://rekayasamesin.ub.ac.id/index.php/rm/article/view/443 |
| _version_ | 1811216152731320320 |
|---|---|
| author | Budiarto Budiarto Kimar Turnip |
| author_facet | Budiarto Budiarto Kimar Turnip |
| author_sort | Budiarto Budiarto |
| collection | DOAJ |
| description | Selection of materials connecting rod for a component or structure usually involves several aspects, there are aspects of specific strength, stiffness, lightweight, noncorrosive materials and resistance or age. In the manufacturing process connecting rod always give heat treatment such as Normalizing, Carburizing, and Induction Tempering. In the process, Induction Tempering has a big problem in hardness after the process, not stable and liable to over from standard. Process condition of tempering induction temperature in 650~700 C at 1 atm pressure, & holding time variation at 5, 10, 15, and 20 seconds. Kind of tests such as bending test, magna-flux, hardness, and structure micro. Bending test report fiber flow is straight, not broke because not found micro crack portension at body connecting rod. Hardness test result min point 23 HRC and max point 39,2 HRC base on standard range 25~44 HRC. The results of surface morphological observation show that the martensite phase causes hardness value to increase. |
| first_indexed | 2024-04-12T06:34:32Z |
| format | Article |
| id | doaj.art-516fb87f8671431399795646c4e1d852 |
| institution | Directory Open Access Journal |
| issn | 2338-1663 2477-6041 |
| language | English |
| last_indexed | 2024-04-12T06:34:32Z |
| publishDate | 2019-01-01 |
| publisher | University of Brawijaya |
| record_format | Article |
| series | Rekayasa Mesin |
| spelling | doaj.art-516fb87f8671431399795646c4e1d8522022-12-22T03:43:54ZengUniversity of BrawijayaRekayasa Mesin2338-16632477-60412019-01-019323523910.21776/ub.jrm.2018.009.03.11342Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 HBudiarto Budiarto0Kimar Turnip1Universitas Kristen IndonesiaUniversitas Kristen IndonesiaSelection of materials connecting rod for a component or structure usually involves several aspects, there are aspects of specific strength, stiffness, lightweight, noncorrosive materials and resistance or age. In the manufacturing process connecting rod always give heat treatment such as Normalizing, Carburizing, and Induction Tempering. In the process, Induction Tempering has a big problem in hardness after the process, not stable and liable to over from standard. Process condition of tempering induction temperature in 650~700 C at 1 atm pressure, & holding time variation at 5, 10, 15, and 20 seconds. Kind of tests such as bending test, magna-flux, hardness, and structure micro. Bending test report fiber flow is straight, not broke because not found micro crack portension at body connecting rod. Hardness test result min point 23 HRC and max point 39,2 HRC base on standard range 25~44 HRC. The results of surface morphological observation show that the martensite phase causes hardness value to increase.http://rekayasamesin.ub.ac.id/index.php/rm/article/view/443SCM 420H SteelsPiston RodInduction TemperingMicrostructure |
| spellingShingle | Budiarto Budiarto Kimar Turnip Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H Rekayasa Mesin SCM 420H Steels Piston Rod Induction Tempering Microstructure |
| title | Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H |
| title_full | Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H |
| title_fullStr | Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H |
| title_full_unstemmed | Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H |
| title_short | Analisis Pengaruh Holding Time terhadap Sifat Mekanis dan Struktur Mikro pada Proses Induction Tempering Batang Piston Baja SCM 420 H |
| title_sort | analisis pengaruh holding time terhadap sifat mekanis dan struktur mikro pada proses induction tempering batang piston baja scm 420 h |
| topic | SCM 420H Steels Piston Rod Induction Tempering Microstructure |
| url | http://rekayasamesin.ub.ac.id/index.php/rm/article/view/443 |
| work_keys_str_mv | AT budiartobudiarto analisispengaruhholdingtimeterhadapsifatmekanisdanstrukturmikropadaprosesinductiontemperingbatangpistonbajascm420h AT kimarturnip analisispengaruhholdingtimeterhadapsifatmekanisdanstrukturmikropadaprosesinductiontemperingbatangpistonbajascm420h |