| Summary: | The quantitative study of rare earth compounds is important for the improvement of existing magnesium alloy systems and the design of new magnesium alloys. In this paper, the effective separation of matrix and compound in Mg–Zn–Ce–Zr alloy was achieved by a low-temperature chemical phase separation technique. The mass fraction of the (Mg, Zn)<sub>12</sub>Ce compound was determined and the effect of the (Mg, Zn)<sub>12</sub>Ce phase content on the heat deformation organization and properties was investigated. The results show that the Mg–Zn–Ce compound in both the as-cast and the homogeneous alloys is (Mg, Zn)<sub>12</sub>Ce. (Mg, Zn)<sub>12</sub>Ce phase formation depends on the content and the ratio of Zn and Ce elements in the initial residual melt of the eutectic reaction. The Zn/Ce mass ratios below 2.5 give the highest compound contents for different Zn contents, 5.262 wt.% and 7.040 wt.%, respectively. The increase in the amount of the (Mg, Zn)<sub>12</sub>Ce phase can significantly reduce the critical conditions for dynamic recrystallization formation. Both the critical strain and the stress decrease with increasing rare earth content. The reduction of the critical conditions and the particle-promoted nucleation mechanism work together to increase the amount of dynamic recrystallization. In addition, it was found that alloys with 6 wt.% Zn elements tend to undergo a dynamic recrystallization softening mechanism, while alloys with 3 wt.% Zn elements tend to undergo a dynamic reversion softening mechanism.
|
|---|