Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives
Abstract The study examined how diatomite and its modifications affected the self-adhesive ability of silicone pressure-sensitive adhesives. To create adhesive composition for testing, fillers were added to a commercial silicone resin, which were then used to create new modified pressure-sensitive t...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Nature Portfolio
2023-08-01
|
| Series: | Scientific Reports |
| Online Access: | https://doi.org/10.1038/s41598-023-40958-0 |
| _version_ | 1827634594220867584 |
|---|---|
| author | Adrian Krzysztof Antosik Karolina Mozelewska Marlena Musik Piotr Miądlicki |
| author_facet | Adrian Krzysztof Antosik Karolina Mozelewska Marlena Musik Piotr Miądlicki |
| author_sort | Adrian Krzysztof Antosik |
| collection | DOAJ |
| description | Abstract The study examined how diatomite and its modifications affected the self-adhesive ability of silicone pressure-sensitive adhesives. To create adhesive composition for testing, fillers were added to a commercial silicone resin, which were then used to create new modified pressure-sensitive tapes. The resulting tapes were tested to determine their adhesion, tack, cohesion at room and elevated temperature, SAFT test (Shear Adhesive Failure Temperature), pot-life (viscosity) and shrinkage. The results obtained were compared with those of the unmodified tapes. The tests resulted in higher thermal resistance (225 °C) and lower shrinkage (0.1%). As a result, we can conclude that materials with thermal resistance with a slight decrease in other parameters were obtained. |
| first_indexed | 2024-03-09T15:16:29Z |
| format | Article |
| id | doaj.art-52e736742a8941bb945370891a4710f4 |
| institution | Directory Open Access Journal |
| issn | 2045-2322 |
| language | English |
| last_indexed | 2024-03-09T15:16:29Z |
| publishDate | 2023-08-01 |
| publisher | Nature Portfolio |
| record_format | Article |
| series | Scientific Reports |
| spelling | doaj.art-52e736742a8941bb945370891a4710f42023-11-26T13:03:55ZengNature PortfolioScientific Reports2045-23222023-08-0113111510.1038/s41598-023-40958-0Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesivesAdrian Krzysztof Antosik0Karolina Mozelewska1Marlena Musik2Piotr Miądlicki3Faculty of Chemical Technology and Engineering, Department of Chemical Organic Technology and Polymeric Materials, West Pomeranian University of Technology, SzczecinFaculty of Chemical Technology and Engineering, Department of Chemical Organic Technology and Polymeric Materials, West Pomeranian University of Technology, SzczecinFaculty of Chemical Technology and Engineering, Department of Chemical Organic Technology and Polymeric Materials, West Pomeranian University of Technology, SzczecinFaculty of Chemical Technology and Engineering, Engineering of Catalytic and Sorbent Materials Department, West Pomeranian University of Technology in SzczecinAbstract The study examined how diatomite and its modifications affected the self-adhesive ability of silicone pressure-sensitive adhesives. To create adhesive composition for testing, fillers were added to a commercial silicone resin, which were then used to create new modified pressure-sensitive tapes. The resulting tapes were tested to determine their adhesion, tack, cohesion at room and elevated temperature, SAFT test (Shear Adhesive Failure Temperature), pot-life (viscosity) and shrinkage. The results obtained were compared with those of the unmodified tapes. The tests resulted in higher thermal resistance (225 °C) and lower shrinkage (0.1%). As a result, we can conclude that materials with thermal resistance with a slight decrease in other parameters were obtained.https://doi.org/10.1038/s41598-023-40958-0 |
| spellingShingle | Adrian Krzysztof Antosik Karolina Mozelewska Marlena Musik Piotr Miądlicki Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives Scientific Reports |
| title | Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives |
| title_full | Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives |
| title_fullStr | Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives |
| title_full_unstemmed | Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives |
| title_short | Influence of diatomite and its base modifications on the self-adhesive properties of silicone pressure-sensitive adhesives |
| title_sort | influence of diatomite and its base modifications on the self adhesive properties of silicone pressure sensitive adhesives |
| url | https://doi.org/10.1038/s41598-023-40958-0 |
| work_keys_str_mv | AT adriankrzysztofantosik influenceofdiatomiteanditsbasemodificationsontheselfadhesivepropertiesofsiliconepressuresensitiveadhesives AT karolinamozelewska influenceofdiatomiteanditsbasemodificationsontheselfadhesivepropertiesofsiliconepressuresensitiveadhesives AT marlenamusik influenceofdiatomiteanditsbasemodificationsontheselfadhesivepropertiesofsiliconepressuresensitiveadhesives AT piotrmiadlicki influenceofdiatomiteanditsbasemodificationsontheselfadhesivepropertiesofsiliconepressuresensitiveadhesives |