Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing
To study the nucleation and recrystallization behavior of deformation bands, shear bands and grain boundaries during the recrystallization process, a heat treatment test was carried out on Cr-Ti-B low-carbon steel after warm rolling and cold rolling. The results show that recrystallization occurs pr...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2022-07-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2075-4701/12/7/1178 |
| _version_ | 1827605008684679168 |
|---|---|
| author | Ankang Huang Zhigang Wang Qiangqiang Yuan Rongchun Chen Jing Qin Yinghui Zhang Weizhen Liu |
| author_facet | Ankang Huang Zhigang Wang Qiangqiang Yuan Rongchun Chen Jing Qin Yinghui Zhang Weizhen Liu |
| author_sort | Ankang Huang |
| collection | DOAJ |
| description | To study the nucleation and recrystallization behavior of deformation bands, shear bands and grain boundaries during the recrystallization process, a heat treatment test was carried out on Cr-Ti-B low-carbon steel after warm rolling and cold rolling. The results show that recrystallization occurs preferentially in shear bands and grain boundaries. The γ deformation texture can be enhanced and the Goss texture can be weakened during the warm rolling and subsequent cold rolling process. Recrystallization of the deformation bands was observed, but the nucleation time of recrystallization in the deformation band is much slower than that in the shear band and grain boundary. |
| first_indexed | 2024-03-09T06:12:35Z |
| format | Article |
| id | doaj.art-53eeff0f6ad44f5ebec34a57086ada67 |
| institution | Directory Open Access Journal |
| issn | 2075-4701 |
| language | English |
| last_indexed | 2024-03-09T06:12:35Z |
| publishDate | 2022-07-01 |
| publisher | MDPI AG |
| record_format | Article |
| series | Metals |
| spelling | doaj.art-53eeff0f6ad44f5ebec34a57086ada672023-12-03T11:56:35ZengMDPI AGMetals2075-47012022-07-01127117810.3390/met12071178Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during AnnealingAnkang Huang0Zhigang Wang1Qiangqiang Yuan2Rongchun Chen3Jing Qin4Yinghui Zhang5Weizhen Liu6Faculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaFaculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaFaculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaFaculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaFaculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaFaculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaFaculty of Material Metallurgy and Chemistry, Jiangxi University of Science and Technology, Ganzhou 341000, ChinaTo study the nucleation and recrystallization behavior of deformation bands, shear bands and grain boundaries during the recrystallization process, a heat treatment test was carried out on Cr-Ti-B low-carbon steel after warm rolling and cold rolling. The results show that recrystallization occurs preferentially in shear bands and grain boundaries. The γ deformation texture can be enhanced and the Goss texture can be weakened during the warm rolling and subsequent cold rolling process. Recrystallization of the deformation bands was observed, but the nucleation time of recrystallization in the deformation band is much slower than that in the shear band and grain boundary.https://www.mdpi.com/2075-4701/12/7/1178Cr-Ti-B low-carbon steelshear bandγ-fiber texturegrain boundarynucleation mechanism |
| spellingShingle | Ankang Huang Zhigang Wang Qiangqiang Yuan Rongchun Chen Jing Qin Yinghui Zhang Weizhen Liu Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing Metals Cr-Ti-B low-carbon steel shear band γ-fiber texture grain boundary nucleation mechanism |
| title | Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing |
| title_full | Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing |
| title_fullStr | Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing |
| title_full_unstemmed | Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing |
| title_short | Recrystallization Behavior of Warm Rolling and Cold Rolling Cr-Ti-B Steel during Annealing |
| title_sort | recrystallization behavior of warm rolling and cold rolling cr ti b steel during annealing |
| topic | Cr-Ti-B low-carbon steel shear band γ-fiber texture grain boundary nucleation mechanism |
| url | https://www.mdpi.com/2075-4701/12/7/1178 |
| work_keys_str_mv | AT ankanghuang recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing AT zhigangwang recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing AT qiangqiangyuan recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing AT rongchunchen recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing AT jingqin recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing AT yinghuizhang recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing AT weizhenliu recrystallizationbehaviorofwarmrollingandcoldrollingcrtibsteelduringannealing |