The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B
In this work, the precipitation of μ phase is detected in alloy 617B during 720 °C aging for 10 000 h. The lattice parameters of μ phase is determined as a = 0.4720–0.4760 nm and c = 2.5394–2.5656 nm in this work. The μ phase in alloy 617B is mainly composed of Mo and Cr, in accompany with Ni and Co...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2019-04-01
|
| Series: | Journal of Materials Research and Technology |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S223878541830591X |
| _version_ | 1819010507937415168 |
|---|---|
| author | He Jiang Jianxin Dong Maicang Zhang |
| author_facet | He Jiang Jianxin Dong Maicang Zhang |
| author_sort | He Jiang |
| collection | DOAJ |
| description | In this work, the precipitation of μ phase is detected in alloy 617B during 720 °C aging for 10 000 h. The lattice parameters of μ phase is determined as a = 0.4720–0.4760 nm and c = 2.5394–2.5656 nm in this work. The μ phase in alloy 617B is mainly composed of Mo and Cr, in accompany with Ni and Co. The chemical formula of μ phase in samples aged for 5000 h and 10 000 h is (Ni0.031Co0.084Cr0.885)2.34Mo and (Ni0.030Co0.091Cr0.879)2.30Mo, respectively. The precipitation of μ phase competes with M23C6 carbide for Cr and Mo elements. Keywords: Nickel-base superalloy, Alloy 617B, μ phase |
| first_indexed | 2024-12-21T01:13:22Z |
| format | Article |
| id | doaj.art-5429481a445a4dbf93b37a146569113d |
| institution | Directory Open Access Journal |
| issn | 2238-7854 |
| language | English |
| last_indexed | 2024-12-21T01:13:22Z |
| publishDate | 2019-04-01 |
| publisher | Elsevier |
| record_format | Article |
| series | Journal of Materials Research and Technology |
| spelling | doaj.art-5429481a445a4dbf93b37a146569113d2022-12-21T19:20:53ZengElsevierJournal of Materials Research and Technology2238-78542019-04-018224612465The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617BHe Jiang0Jianxin Dong1Maicang Zhang2Corresponding author.; School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing, 100083, ChinaSchool of Materials Science and Engineering, University of Science and Technology Beijing, Beijing, 100083, ChinaSchool of Materials Science and Engineering, University of Science and Technology Beijing, Beijing, 100083, ChinaIn this work, the precipitation of μ phase is detected in alloy 617B during 720 °C aging for 10 000 h. The lattice parameters of μ phase is determined as a = 0.4720–0.4760 nm and c = 2.5394–2.5656 nm in this work. The μ phase in alloy 617B is mainly composed of Mo and Cr, in accompany with Ni and Co. The chemical formula of μ phase in samples aged for 5000 h and 10 000 h is (Ni0.031Co0.084Cr0.885)2.34Mo and (Ni0.030Co0.091Cr0.879)2.30Mo, respectively. The precipitation of μ phase competes with M23C6 carbide for Cr and Mo elements. Keywords: Nickel-base superalloy, Alloy 617B, μ phasehttp://www.sciencedirect.com/science/article/pii/S223878541830591X |
| spellingShingle | He Jiang Jianxin Dong Maicang Zhang The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B Journal of Materials Research and Technology |
| title | The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B |
| title_full | The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B |
| title_fullStr | The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B |
| title_full_unstemmed | The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B |
| title_short | The characteristics of μ phase precipitated during 720 °C long-term aging in alloy 617B |
| title_sort | characteristics of μ phase precipitated during 720 °c long term aging in alloy 617b |
| url | http://www.sciencedirect.com/science/article/pii/S223878541830591X |
| work_keys_str_mv | AT hejiang thecharacteristicsofmphaseprecipitatedduring720clongtermaginginalloy617b AT jianxindong thecharacteristicsofmphaseprecipitatedduring720clongtermaginginalloy617b AT maicangzhang thecharacteristicsofmphaseprecipitatedduring720clongtermaginginalloy617b AT hejiang characteristicsofmphaseprecipitatedduring720clongtermaginginalloy617b AT jianxindong characteristicsofmphaseprecipitatedduring720clongtermaginginalloy617b AT maicangzhang characteristicsofmphaseprecipitatedduring720clongtermaginginalloy617b |