Effect Of Heat-Treatment On Microstructure And Magnetic Properties Of Nanocrystallized Mn-Zn Ferrite Powders
The initial ferrite powders were subjected to high energy ball milling at 300rpm for 3h, and subsequently heat-treated at 573-1273K for 1h. Based on the observation of microstructure and measurement of magnetic properties, the heat-treatment effect was investigated. The size of initial powders was a...
Main Authors: | Lee W.H., Hong C.S., Chang S.Y. |
---|---|
Format: | Article |
Language: | English |
Published: |
Polish Academy of Sciences
2015-06-01
|
Series: | Archives of Metallurgy and Materials |
Subjects: | |
Online Access: | http://www.degruyter.com/view/j/amm.2015.60.issue-2/amm-2015-0128/amm-2015-0128.xml?format=INT |
Similar Items
-
Microstructure Evolution of Ni-Based ODS Superalloy Powders During Horizontal Rotary Ball Milling
by: Lee H.-E., et al.
Published: (2017-06-01) -
Mechano-chemical activation of MoO3-CuO/C powder mixture to synthesis nano crystalline Mo-Cu alloy
by: Morteza Saghafi Yazdi, et al.
Published: (2018-12-01) -
Modeling the particle size of nanomaterials synthesized in a planetary ball mill
by: Chwadaka Pohshna, et al.
Published: (2023-11-01) -
Influence of Process Control Agent on Characterization and Structure of Micron Chitosan Powders Prepared by Ball Milling Method
by: ZHANG Chuan-jie, et al.
Published: (2016-12-01) -
Microstructure and magnetic properties of MnBi powders prepared by various ball milling processes
by: Chengyu Li, et al.
Published: (2024-01-01)