| Summary: | The uniform and smaller-sized (~3 μm) LiNi<sub>0.8</sub>Co<sub>0.1</sub>Mn<sub>0.1</sub>O<sub>2</sub> (SNCM) particles are prepared via a fast nucleation process of oxalate co-precipitation, followed by a two-step calcination procedure. It is found that the fast nucleation by vigorous agitation enables us to produce oxalate nuclei having a uniform size which then grow into micron-particles in less than a few minutes. The impacts of solution pH, precipitation time, calcination temperature, and surface modification with ZrO<sub>2</sub> on the structural, morphological, and electrochemical properties of SNCM are systematically examined to identify the optimal synthetic conditions. A novel bimodal cathode design has been highlighted by using the combination of the SNCM particles and the conventional large (~10 μm) LiNi<sub>0.83</sub>Co<sub>0.12</sub>Mn<sub>0.05</sub>O<sub>2</sub> (LNCM) particles to achieve the high volumetric energy density of cathode. The volumetric discharge capacity is found to be 526.6 mAh/cm<sup>3</sup> for the bimodal cathode L80% + S20%, whereas the volumetric discharge capacity is found to be only 480.3 and 360.6 mAh/cm<sup>3</sup> for L100% and S100% unimodal, respectively. Moreover, the optimal bi-modal cathode delivered higher specific energy (622.4 Wh/kg) and volumetric energy density (1622.6 Wh/L) than the L100% unimodal (596.1 Wh/kg and 1402.1 Wh/L) cathode after the 100th cycle. This study points to the promising utility of the SNCM material in Li-ion battery applications.
|
|---|