| Summary: | In additive manufacturing technologies, fused deposition modelling (FDM) is continuing its advancement from rapid prototyping to rapid manufacturing. However, effective usage of FDM is not performed due to the poor mechanical properties of the 3D-printed components. This drawback restricts their usage in many applications. Much research, such as reinforcing 3D-printed parts with fibers, changing printing parameters (infill density, infill concentration, extrusion temperature, nozzle diameter, layer thickness, raster angle, etc.) are aimed to increase the mechanical properties of 3D-printed parts. This research paper aims to investigate the effect of pressure and temperature on the mechanical properties and consolidation of layers of 3D-printed PLA (Polylactic Acid). Post-treatment was done using a customized autoclave. Autoclave has the capability to maintain 185 °C and 135 bar pressure. Three-dimensional-printed specimens were manufactured using the FDM process with two patterns. Later, the specimens were subjected to various post-treatment processes, then followed with testing and analysis of mechanical properties. Post-treatment process carried out by placing them in an autoclave at certain pressure and temperature conditions. To investigate the repeatability and tolerances, the test series includes a minimum of four to six test specimens. The results indicate that the concentric pattern yields the most desirable tensile, impact, and flexural strength due to the alignment of deposited rasters and better consolidation of layers with the loading direction. The pressure and temperature of the autoclave has a positive effect on the PLA samples, which helped them to reorganize the structure, hence strength properties were enhanced. The test results also compared with injection-molded samples for better understating.
|
|---|