Corrosion Activity of Carbon Steel B450C and Low Chromium Ferritic Stainless Steel 430 in Cement Extract Solution
This study compares corrosion activities of carbon steel B450C and SS 430 (Mn in low content) exposed for 30 days in cement extract solution. Iron oxide and hydroxide were formed as corrosion products, in addition to CaCO<sub>3</sub>, in the presence of Cr<sub>2</sub>O<sub...
Main Authors: | Ángel Bacelis, Lucien Veleva, Sebastián Feliu, Marina Cabrini, Sergio Lorenzi |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-05-01
|
Series: | Buildings |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-5309/11/6/220 |
Similar Items
-
Corrosion Activity of Carbon Steel B450C and Low Chromium Ferritic Stainless Steel 430 in Chloride-Containing Cement Extract Solution
by: Lucien Veleva, et al.
Published: (2022-01-01) -
Corrosion Activity of Carbon Steel B450C and Stainless Steel SS430 Exposed to Extract Solution of a Supersulfated Cement
by: David Bonfil, et al.
Published: (2022-12-01) -
Corrosion Activity of Stainless Steel SS430 and Carbon Steel B450C in a Sodium Silicate Modified Limestone-Portland Cement Extract
by: David Bonfil, et al.
Published: (2023-07-01) -
Advances in stainless steels /
by: Raj, Baldev, 1947-, et al.
Published: (2009) -
Welding metallurgy of stainless steels/
by: 203435 Folkhard, Erich
Published: (1988)