| Summary: | The characteristics of acid-activated raw bentonite (RB) activated with binary acid solutions sulfuric acid + nitric acid, nitric acid + phosphoric acid, and phosphoric acid + sulfuric acid, at a concentration of 5 mol/L (denoted as 5-SN, 5-NP, and 5-PS), were evaluated. Moreover, its application for improving the electrical conductivity in tap water was demonstrated. Acid activation induced the partial destruction of RB; subsequently, there was a significant release of sodium ions from the RB. In addition, the specific surface area and pore volume of 5-SN, 5-NP, and 5-PS were higher than those of RB. Next, the electrical conductivity when using RB increased with adsorption treatment because sodium ions were released from the RB. However, the electrical conductivity significantly decreased with adsorption treatment when using acid-activated RB. Specifically, magnesium ions, calcium ions, and potassium ions were removed into 5-SN, 5-NP, and 5-PS, and sodium ions were not released from the RB simultaneously. The removal percentage of the electrical conductivity using 5-SN, 5-NP, and 5-PS was approximately 31% to 36%. The results indicated that employing acid-activated RB with a binary acid solution is a useful method for decreasing the electrical conductivity in tap water.
|
|---|