| Summary: | In this work, the influence of spray parameters on the formation of the microstructure, phase composition, and the tribological properties of detonation flame sprayed coatings was studied. It was determined that the chemical composition of Cr3C2-NiCr coatings during detonation spraying depends on the degree of filling the barrel with an explosive gas mixture. The degree of filling the barrel with an explosive gas mixture at 73% leads to a decrease in the content of carbide phases, and at 57% filling of the barrel, an increase in carbide phases is observed. It is established that the decrease of the filling degree leads to the increase of hardness and wear resistance of the Cr3C2-NiCr coatings since the hardness and wear resistance of the coating material deposited at 57% is higher than at 65% and 73%; this is due to the increase in the carbide phase Cr3C2. Detonation flame sprayed Cr3C2-NiCr gradient coatings have been developed in this study, which is carried out by varying the spray parameters. It was found that in the gradient coating, Cr3C2-NiCr carbide phases gradually increase from the depth to the surface. The obtained gradient coating closer to the substrate consists of the CrNi3 phase, while the coating surface consists of CrNi3 and Cr3C2 phases.
|
|---|