Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings
In this work, the influence of spray parameters on the formation of the microstructure, phase composition, and the tribological properties of detonation flame sprayed coatings was studied. It was determined that the chemical composition of Cr3C2-NiCr coatings during detonation spraying depends on th...
Main Authors: | , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Hindawi Limited
2023-01-01
|
Series: | Advances in Tribology |
Online Access: | http://dx.doi.org/10.1155/2023/6684656 |
_version_ | 1797850571710922752 |
---|---|
author | Bauyrzhan Rakhadilov Dauir Kakimzhanov Merkhat Dautbekov Zhuldyz Sagdoldina Meruyert Adylkanova Riza Abylkalykova |
author_facet | Bauyrzhan Rakhadilov Dauir Kakimzhanov Merkhat Dautbekov Zhuldyz Sagdoldina Meruyert Adylkanova Riza Abylkalykova |
author_sort | Bauyrzhan Rakhadilov |
collection | DOAJ |
description | In this work, the influence of spray parameters on the formation of the microstructure, phase composition, and the tribological properties of detonation flame sprayed coatings was studied. It was determined that the chemical composition of Cr3C2-NiCr coatings during detonation spraying depends on the degree of filling the barrel with an explosive gas mixture. The degree of filling the barrel with an explosive gas mixture at 73% leads to a decrease in the content of carbide phases, and at 57% filling of the barrel, an increase in carbide phases is observed. It is established that the decrease of the filling degree leads to the increase of hardness and wear resistance of the Cr3C2-NiCr coatings since the hardness and wear resistance of the coating material deposited at 57% is higher than at 65% and 73%; this is due to the increase in the carbide phase Cr3C2. Detonation flame sprayed Cr3C2-NiCr gradient coatings have been developed in this study, which is carried out by varying the spray parameters. It was found that in the gradient coating, Cr3C2-NiCr carbide phases gradually increase from the depth to the surface. The obtained gradient coating closer to the substrate consists of the CrNi3 phase, while the coating surface consists of CrNi3 and Cr3C2 phases. |
first_indexed | 2024-04-09T19:02:30Z |
format | Article |
id | doaj.art-5cc5ef7472ff47eb8ff5083fa9951b57 |
institution | Directory Open Access Journal |
issn | 1687-5923 |
language | English |
last_indexed | 2024-04-09T19:02:30Z |
publishDate | 2023-01-01 |
publisher | Hindawi Limited |
record_format | Article |
series | Advances in Tribology |
spelling | doaj.art-5cc5ef7472ff47eb8ff5083fa9951b572023-04-08T00:00:05ZengHindawi LimitedAdvances in Tribology1687-59232023-01-01202310.1155/2023/6684656Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation CoatingsBauyrzhan Rakhadilov0Dauir Kakimzhanov1Merkhat Dautbekov2Zhuldyz Sagdoldina3Meruyert Adylkanova4Riza Abylkalykova5PlasmaScience LLPPlasmaScience LLPD.Serikbaev East Kazakhstan Technical UniversitySarsen Amanzholov East Kazakhstan UniversityD.Serikbaev East Kazakhstan Technical UniversitySarsen Amanzholov East Kazakhstan UniversityIn this work, the influence of spray parameters on the formation of the microstructure, phase composition, and the tribological properties of detonation flame sprayed coatings was studied. It was determined that the chemical composition of Cr3C2-NiCr coatings during detonation spraying depends on the degree of filling the barrel with an explosive gas mixture. The degree of filling the barrel with an explosive gas mixture at 73% leads to a decrease in the content of carbide phases, and at 57% filling of the barrel, an increase in carbide phases is observed. It is established that the decrease of the filling degree leads to the increase of hardness and wear resistance of the Cr3C2-NiCr coatings since the hardness and wear resistance of the coating material deposited at 57% is higher than at 65% and 73%; this is due to the increase in the carbide phase Cr3C2. Detonation flame sprayed Cr3C2-NiCr gradient coatings have been developed in this study, which is carried out by varying the spray parameters. It was found that in the gradient coating, Cr3C2-NiCr carbide phases gradually increase from the depth to the surface. The obtained gradient coating closer to the substrate consists of the CrNi3 phase, while the coating surface consists of CrNi3 and Cr3C2 phases.http://dx.doi.org/10.1155/2023/6684656 |
spellingShingle | Bauyrzhan Rakhadilov Dauir Kakimzhanov Merkhat Dautbekov Zhuldyz Sagdoldina Meruyert Adylkanova Riza Abylkalykova Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings Advances in Tribology |
title | Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings |
title_full | Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings |
title_fullStr | Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings |
title_full_unstemmed | Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings |
title_short | Influence of Spraying Parameters on the Structure and Tribological Properties of Cr3C2-NiCr Detonation Coatings |
title_sort | influence of spraying parameters on the structure and tribological properties of cr3c2 nicr detonation coatings |
url | http://dx.doi.org/10.1155/2023/6684656 |
work_keys_str_mv | AT bauyrzhanrakhadilov influenceofsprayingparametersonthestructureandtribologicalpropertiesofcr3c2nicrdetonationcoatings AT dauirkakimzhanov influenceofsprayingparametersonthestructureandtribologicalpropertiesofcr3c2nicrdetonationcoatings AT merkhatdautbekov influenceofsprayingparametersonthestructureandtribologicalpropertiesofcr3c2nicrdetonationcoatings AT zhuldyzsagdoldina influenceofsprayingparametersonthestructureandtribologicalpropertiesofcr3c2nicrdetonationcoatings AT meruyertadylkanova influenceofsprayingparametersonthestructureandtribologicalpropertiesofcr3c2nicrdetonationcoatings AT rizaabylkalykova influenceofsprayingparametersonthestructureandtribologicalpropertiesofcr3c2nicrdetonationcoatings |