| Summary: | The one-dimensional (1D) polyethylene (PE) nanocrystals were generated in epoxy thermosets via crystallization-driven self-assembly. Toward this end, an ABA triblock copolymer composed of PE midblock and poly(ε-caprolactone) (PCL) endblocks was synthesized via the ring opening metathesis polymerization followed by hydrogenation approach. The nanostructured thermosets were obtained via a two-step curing approach, i.e., the samples were cured first at 80 °C and then at 150 °C. Under this condition, the one-dimensional (1D) fibrous PE microdomains with the lengths up to a couple of micrometers were created in epoxy thermosets. In contrast, only the spherical PE microdomains were generated while the thermosets were cured via a one-step curing at 150 °C. By the use of the triblock copolymer, the generation of 1D fibrous PE nanocrystals is attributable to crystallization-driven self-assembly mechanism whereas that of the spherical PE microdomains follows traditional self-assembly mechanism. Compared to the thermosets containing the spherical PE microdomains, the thermosets containing the 1D fibrous PE nanocrystals displayed quite different thermal and mechanical properties. More importantly, the nanostructured thermosets containing the 1D fibrous PE nanocrystals displayed the fracture toughness much higher than those only containing the spherical PE nanocrystals; the K<sub>IC</sub> value was even three times as that of control epoxy.
|
|---|