Impact of Zn2+-Zr4+ substitution on M-type Barium Strontium Hexaferrite’s structural, surface morphology, dielectric and magnetic properties

Impact of Zn2+-Zr4+ substitution on M-type Barium Strontium Hexaferrite’s structural, surface morphology, dielectric and magnetic properties

We report the synthesis of Ba0.5Sr0.5ZnxZrxFe12-2xO19 (x = 0.00–1.00) samples using sol–gel auto combustion method. The Rietveld refinement of XRD data indicates a) pure phase formation, b) increase in lattice parameters with composition and c) the absence of undesirable phases such as α–Fe2O3, BaCO...

সম্পূর্ণ বিবরণ

গ্রন্থ-পঞ্জীর বিবরন
প্রধান লেখক: Sachin Kumar Godara, Varinder Kaur, Kirti Chuchra, S.B. Narang, Gurpreet Singh, Mandeep singh, Aanchal chawla, Swati Verma, Gopala Ram Bhadu, Jayesh C. Chaudhari, P.D. Babu, Ashwani Kumar Sood
বিন্যাস: প্রবন্ধ
ভাষা:English
প্রকাশিত: Elsevier 2021-03-01
মালা:Results in Physics
বিষয়গুলি:
Barium Strontium Hexaferrite
Raman
Rietveld refinement
Coercivity
Magnetic recording
অনলাইন ব্যবহার করুন:http://www.sciencedirect.com/science/article/pii/S2211379721000723