PEROVSKITES BOOSTED BY METAL OXIDES AS A CATALYST FOR THE PARTIAL OXIDATION OF METHANE

This research aims to study the comprehensive identification of the synthesis, characterisation and performance tests of La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) and La0.7Sr0.3MnO3-δ (LSM) granule-form catalysts with a CeO₂ and NiO addition for the POM reaction. The LSCF and LSM powder were firstly prepared...

Full description

Bibliographic Details
Main Authors: Silvana Dwi Nurherdiana, Nurul Widiastuti, Gunawan Triyanda, Lestari Witri Wahyu, Mukti Rino Rakhmata, Fansuri Hamzah
Format: Article
Language:English
Published: University of Chemistry and Technology, Prague 2022-03-01
Series:Ceramics-Silikáty
Subjects:
Online Access: http://www.ceramics-silikaty.cz/index.php?page=cs_detail_doi&id=1491
Description
Summary:This research aims to study the comprehensive identification of the synthesis, characterisation and performance tests of La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) and La0.7Sr0.3MnO3-δ (LSM) granule-form catalysts with a CeO₂ and NiO addition for the POM reaction. The LSCF and LSM powder were firstly prepared using the solid-state reaction method. The granules were firstly prepared in a form of pellet, then crushed and sieved into a size of ± 1mm. The performance study begins with a pre-treated process, by flowing 5% O₂ gas (30 mL.min-1) in the fixed-bed reactor at 600 °C. The product was analysed using Agilent HP 6890 gas chromatography equipped with an Agilent HP 19095P-Q04 column and a FID detector. The results showed that the LSCF achieved 50.03% methane conversion which is lower than the LSM performance of 56.41%. The CeO₂ addition in both the LSCF and LSM revealed an increasing performance by increasing the reaction time. NiO addition resulted in a slower increase in the reaction time, which can be caused by the rate of carbon deposition formation. Based on the obtained results, the bifunctional catalyst has the potential to be developed into another module with a larger effective surface area, such as a multiple-thin layer membrane or hollow fibre membrane.