STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR
Bending fatigue failure is one of the main failure modes for gears in transmission system, shot peening is an important gear strengthen technology. In order to study the influence of shot peening on gear bending fatigue characteristics, 20 MnCr5 carburized involute cylindrical spur gear was adopted...
| Autors principals: | , , , , , |
|---|---|
| Format: | Article |
| Idioma: | zho |
| Publicat: |
Editorial Office of Journal of Mechanical Strength
2022-01-01
|
| Col·lecció: | Jixie qiangdu |
| Matèries: | |
| Accés en línia: | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2022.05.07 |
| _version_ | 1826870664723693568 |
|---|---|
| author | ZHAO HongQiao XIAO JiSheng ZHONG ZhenYuan WANG Rong LUO WeiXian HU JianSun |
| author_facet | ZHAO HongQiao XIAO JiSheng ZHONG ZhenYuan WANG Rong LUO WeiXian HU JianSun |
| author_sort | ZHAO HongQiao |
| collection | DOAJ |
| description | Bending fatigue failure is one of the main failure modes for gears in transmission system, shot peening is an important gear strengthen technology. In order to study the influence of shot peening on gear bending fatigue characteristics, 20 MnCr5 carburized involute cylindrical spur gear was adopted as study object. The effect of shot peening on gear surface integrity were analyzed before and after shot peening, coinciding with our products. Bending fatigue test was carried out with the single tooth loading method, afterwards, based on the observation of the failure fracture surfaces by scanning electron microscope（SEM）, the differences of failure characteristics in the crack source areas before and after shot peening were analyzed. It is found that shot peening can greatly improve gear surface integrity, although it has a negative effect on the gear surface corrugation. Shot peening can effectively increase gear bending strength and restrain the crack initiation from the gear surface. |
| first_indexed | 2024-03-12T20:42:06Z |
| format | Article |
| id | doaj.art-6294f98de01947aabc1c41e901b62b59 |
| institution | Directory Open Access Journal |
| issn | 1001-9669 |
| language | zho |
| last_indexed | 2025-02-16T23:27:58Z |
| publishDate | 2022-01-01 |
| publisher | Editorial Office of Journal of Mechanical Strength |
| record_format | Article |
| series | Jixie qiangdu |
| spelling | doaj.art-6294f98de01947aabc1c41e901b62b592025-01-15T02:39:17ZzhoEditorial Office of Journal of Mechanical StrengthJixie qiangdu1001-96692022-01-01441064106831951200STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEARZHAO HongQiaoXIAO JiShengZHONG ZhenYuanWANG RongLUO WeiXianHU JianSunBending fatigue failure is one of the main failure modes for gears in transmission system, shot peening is an important gear strengthen technology. In order to study the influence of shot peening on gear bending fatigue characteristics, 20 MnCr5 carburized involute cylindrical spur gear was adopted as study object. The effect of shot peening on gear surface integrity were analyzed before and after shot peening, coinciding with our products. Bending fatigue test was carried out with the single tooth loading method, afterwards, based on the observation of the failure fracture surfaces by scanning electron microscope（SEM）, the differences of failure characteristics in the crack source areas before and after shot peening were analyzed. It is found that shot peening can greatly improve gear surface integrity, although it has a negative effect on the gear surface corrugation. Shot peening can effectively increase gear bending strength and restrain the crack initiation from the gear surface.http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2022.05.0720MnCr5 carburized gearShot peeningGear surface integrityBending fatigue characteristicsFailure fracture surfaces observation |
| spellingShingle | ZHAO HongQiao XIAO JiSheng ZHONG ZhenYuan WANG Rong LUO WeiXian HU JianSun STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR Jixie qiangdu 20MnCr5 carburized gear Shot peening Gear surface integrity Bending fatigue characteristics Failure fracture surfaces observation |
| title | STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR |
| title_full | STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR |
| title_fullStr | STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR |
| title_full_unstemmed | STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR |
| title_short | STUDY ON THE INFLUENCE OF SHOT PEENING ON THE BENDING FATIGUE CHARACTERISTICS OF 20MNCR5 CARBURIZED GEAR |
| title_sort | study on the influence of shot peening on the bending fatigue characteristics of 20mncr5 carburized gear |
| topic | 20MnCr5 carburized gear Shot peening Gear surface integrity Bending fatigue characteristics Failure fracture surfaces observation |
| url | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2022.05.07 |
| work_keys_str_mv | AT zhaohongqiao studyontheinfluenceofshotpeeningonthebendingfatiguecharacteristicsof20mncr5carburizedgear AT xiaojisheng studyontheinfluenceofshotpeeningonthebendingfatiguecharacteristicsof20mncr5carburizedgear AT zhongzhenyuan studyontheinfluenceofshotpeeningonthebendingfatiguecharacteristicsof20mncr5carburizedgear AT wangrong studyontheinfluenceofshotpeeningonthebendingfatiguecharacteristicsof20mncr5carburizedgear AT luoweixian studyontheinfluenceofshotpeeningonthebendingfatiguecharacteristicsof20mncr5carburizedgear AT hujiansun studyontheinfluenceofshotpeeningonthebendingfatiguecharacteristicsof20mncr5carburizedgear |