Enhancing the fracture properties of carbon fiber-calcium silicate hydrate interface through graphene oxide
As a quasi-brittle material, concrete's toughness and durability are significantly affected by cracking. Extensive research has been focused on fiber reinforcing, a popular way to enhance concrete's mechanical properties. The bonding performance of the fiber–matrix interface plays a critic...
Main Authors: | Benzhi Min, Guoliang Chen, Yongyang Sun, Ke Li, Xi Chen, Zhenqing Wang |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2024-05-01
|
Series: | Materials & Design |
Online Access: | http://www.sciencedirect.com/science/article/pii/S0264127524002892 |
Similar Items
-
Interactions between Reduced Graphene Oxide with Monomers of (Calcium) Silicate Hydrates: A First-Principles Study
by: Mohammadreza Izadifar, et al.
Published: (2021-08-01) -
Impacts of Space Restriction on the Microstructure of Calcium Silicate Hydrate
by: Yue Zhou, et al.
Published: (2021-06-01) -
Structure, Fractality, Mechanics and Durability of Calcium Silicate Hydrates
by: Shengwen Tang, et al.
Published: (2021-05-01) -
Tuning the Hydration Acceleration Efficiency of Calcium Carbonate by Pre-Seeding with Calcium Silicate Hydrate
by: Han Yan, et al.
Published: (2022-09-01) -
Molecular Dynamics Study on Mechanical Properties of Interface between Urea-Formaldehyde Resin and Calcium-Silicate-Hydrates
by: Xianfeng Wang, et al.
Published: (2020-09-01)