| Summary: | The aim of this study was to utilize cassava pulp to prepare biocomposites comprising microcrystalline cellulose from cassava pulp (CP-MCC) as a filler and polyhydroxybutyrate (PHB) synthesized in-house by Cupriavidus necator strain A-04. The CP-MCC was extracted from fresh cassava pulp. Next, the CP-MCC surface was modified with butyryl chloride (esterified to CP-MCC butyrate) to improve dissolution and compatibility with the PHB. FTIR results confirmed that the esterified CP-MCC butyrate had aliphatic chains replacing the hydroxyl groups; this substitution increased the solubilities in acetone, chloroform, and tetrahydrofuran. Biocomposite films were prepared by varying the composition of esterified CP-MCC butyrate as a filler in the PHB matrix at 0, 5, 10, 15, 20 and 100 wt%. The results for the 95:5 and 90:10 CP-MCC butyrate biocomposite films showed that esterification led to improvements in the thermal properties and increased tensile strengths and elongations at break. All prepared biocomposite films maintained full biodegradability.
|
|---|