Oxidation behavior of Si3N4-TiN composites at 1400 oC
In this paper, the oxidation behavior of silicon nitride with different contents of TiN was evaluated at 1400 oC for 64 hours in air. The oxidized samples were characterized by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy. Weight gain measurements have sho...
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2023-11-01
|
Series: | Materials Research |
Subjects: | |
Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392023000100313&lng=en&tlng=en |
Summary: | In this paper, the oxidation behavior of silicon nitride with different contents of TiN was evaluated at 1400 oC for 64 hours in air. The oxidized samples were characterized by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy. Weight gain measurements have shown that the oxidation followed a multiple-law model with linear, parabolic, and logarithmic contributions. The samples presented high weight gain at the beginning of the process followed by the formation of an amorphous silica surface layer containing Y2Ti2O7 and rutile crystals. Cracks and holes were detected on the oxide layer. The oxidation resistance of the composites was strongly influenced by the initial content of TiN. |
---|---|
ISSN: | 1516-1439 |