A Novel Non-Equiatomic (W<sub>35</sub>Ta<sub>35</sub>Mo<sub>15</sub>Nb<sub>15</sub>)<sub>95</sub>Ni<sub>5</sub> Refractory High Entropy Alloy with High Density Fabricated by Powder Metallurgical Process
A non-equiatomic refractory high entropy alloy (RHEA), (W<sub>35</sub>Ta<sub>35</sub>Mo<sub>15</sub>Nb<sub>15</sub>)<sub>95</sub>Ni<sub>5</sub> with high density of 14.55 g/cm<sup>3</sup> was fabricated by powder met...
Main Authors: | Bohua Duan, Yingrui Yu, Xinli Liu, Dezhi Wang, Zhuangzhi Wu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-10-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/10/11/1436 |
Similar Items
-
Effect of Homogenization on the Transformation Temperatures and Mechanical Properties of Cu<sub>15</sub>Ni<sub>35</sub>Hf<sub>12.5</sub>Ti<sub>25</sub>Zr<sub>12.5</sub> and Cu<sub>15</sub>Ni<sub>35</sub>Hf<sub>15</sub>Ti<sub>20</sub>Zr<sub>15</sub> High-Entropy Shape Memory Alloys
by: Shu-Yu Kuo, et al.
Published: (2023-04-01) -
Microstructure and Mechanical Properties of Precipitate Strengthened High Entropy Alloy Al<sub>10</sub>Co<sub>25</sub>Cr<sub>8</sub>Fe<sub>15</sub>Ni<sub>36</sub>Ti<sub>6</sub> with Additions of Hafnium and Molybdenum
by: Sebastian Haas, et al.
Published: (2019-02-01) -
Microstructure and Magnetic Properties of Nanocrystalline Fe<sub>60−x</sub>Co<sub>25</sub>Ni<sub>15</sub>Si<sub>x</sub> Alloy Elaborated by High-Energy Mechanical Milling
by: Nawel Khitouni, et al.
Published: (2022-09-01) -
Influence of Hafnium Addition on the Microstructure, Microhardness and Corrosion Resistance of Ti<sub>20</sub>Ta<sub>20</sub>Nb<sub>20</sub>(ZrMo)<sub>20−x</sub>Hf<sub>x</sub> (where x = 0, 5, 10, 15 and 20 at.%) High Entropy Alloys
by: Karsten Glowka, et al.
Published: (2023-02-01) -
Microstructures, Mechanical Properties and Transformation Behavior in Ni<sub>49.6</sub>Ti<sub>35.4</sub>Hf<sub>15</sub> Alloy Produced with High-Pressure Torsion
by: Jintao Zhang, et al.
Published: (2023-08-01)