Nano-Hybrids Based on Surface Modified Reduced Graphene Oxide Nanosheets and Carbon Nanotubes and a Regioregular Polythiophene
The multi-walled carbon nanotubes (CNTs) and reduced graphene oxide (rGO) nanosheets were functionalized with 2-hydroxymethyl thiophene (CNT-f-COOTh) and 2-thiophene acetic acid (rGO-f-TAA) and grafted with poly(3-dodecylthiophene) (CNT-g-PDDT and rGO-g-PDDT) to manipulate the orientation and patter...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Tehran
2018-06-01
|
| Series: | Journal of Ultrafine Grained and Nanostructured Materials |
| Subjects: | |
| Online Access: | https://jufgnsm.ut.ac.ir/article_65969_1752fdceafd6045324fdbcae5c5c4eb9.pdf |
| Summary: | The multi-walled carbon nanotubes (CNTs) and reduced graphene oxide (rGO) nanosheets were functionalized with 2-hydroxymethyl thiophene (CNT-f-COOTh) and 2-thiophene acetic acid (rGO-f-TAA) and grafted with poly(3-dodecylthiophene) (CNT-g-PDDT and rGO-g-PDDT) to manipulate the orientation and patterning of crystallized regioregular poly(3-hexylthiophene) (P3HT). Distinct nano-hybrid structures including double-fibrillar (5.11−5.18 S/cm), shish-kebab (2.19−2.28 S/cm), and stem-leaf (6.96−7.51 S/cm) were developed using modified CNTs and P3HT. The most effective parameter on morphology of donor-acceptor supramolecules was the surface functionalization and grafting. The electrical conductivities of supramolecules based on P3HT and rGO, rGO-f-TAA, and rGO-g-PDDT ranged in 3.81−3.87, 3.91−3.95, and 10.67−10.70 S/cm, respectively. P3HT chains preferred to interact with their thiophene rings with bared rGO and CNT surfaces, resulting in a conventional face-on orientation. In P3HT/rGO-f-TAA and P3HT/CNT-f-COOTh supramolecular nanostructures patterned with P3HT, the orientation of P3HT chains changed from face-on to edge-on, originating from the strong interactions between the hexyl side chains of P3HTs and functional groups. Nano-hybrids based on grafted rGO demonstrated a patched-like morphology composed of flat-on P3HTs with main backbones perpendicular to the substrate. Based on the ultraviolet-visible and photoluminescence analyses, the flat-on orientation was the best for P3HT chains assembled onto CNT and rGO, which was acquired for CNT-g-PDDT and rGO-g-PDDT nano-hybrids. |
|---|---|
| ISSN: | 2423-6845 2423-6837 |